PA66，LNP™ THERMOCOMP™ Compound RC008H对比PA66，Electrafil® PA6/6 CF40 BK物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ Compound RC008H 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Electrafil® PA6/6 CF40 BK 物性表 PA66 & 美国Techmer 指导价格：暂无塑料库存：缺货
牌号简介	LNP ThermocompRC008H是一种基于尼龙66树脂的化合物，含有40%的碳纤维。这种材料的附加功能包括：导电、保健。 LNP THERMOCOMP RC008H is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.	Electrafil® PA6/6 CF40 BK是一种聚酰胺66（尼龙66）产品,含有的填充物为40% 碳纤维增强材料。它可以通过注射成型进行加工,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 Electrafil® PA6/6 CF40 BK的应用领域包括包装、工程/工业配件、汽车行业、商业/办公用品和输送带。特性包括: 阻燃/额定火焰通过 ROHS 认证传导性 Electrafil® PA6/6 CF40 BK is a Polyamide 66 (Nylon 66) product filled with 40% carbon fiber. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Electrafil® PA6/6 CF40 BK include automotive, business/office goods, conveyors, engineering/industrial parts and packaging. Characteristics include: Flame Rated RoHS Compliant Conductive

产品描述
厂家：	沙特沙伯基础 SABIC	美国Techmer
类别：	PA66 PA66	PA66 PA66
填料：	碳纤维 40	碳纤维 40
用途：	电气/电子应用领域,医疗/护理用品,石油/天然气用品	衬套,传送机配件,汽车电子,包装,商务设备
性能特点：	导电 Conductive	导电,抗静电 Conductive,Antistatic property
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate %

机械性能
MECHANICAL LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(断裂，100 mm跨度)
bending strength MPa ASTM D790

弯曲模量(100 mm跨距)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

抗张强度(断裂)
Tensile strength (fracture) MPa ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃，3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23°C，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

电气性能
ELECTRICAL LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

补充信息
LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位
UNIT 测试方法
TEST METHOD

加工方式

注射 LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆转速 rpm

注射说明 LNP™ THERMOCOMP™ Compound RC008H Electrafil® PA6/6 CF40 BK 单位测试方法

备注

2、5.0 mm/min

3、类型 1, 5.0 mm/min

4、2.6 mm/min

5、80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
注射说明
备注