PES，Veradel® 3300 SL30对比PES，LNP™ LUBRICOMP™ JZL012 compound物性表,价格行情_搜料

牌号信息	Veradel® 3300 SL30 物性表 PES & 比利时索尔维指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ JZL012 compound 物性表 PES & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Veradel® 3300 SL30是一种聚醚砜（PESU）化合物，设计用于在干燥和外部润滑应用中提供优良的机械性能、耐磨性和低摩擦系数的平衡。该树脂由碳纤维、石墨和聚四氟乙烯（PTFE）组成的三元抗摩擦/耐磨添加剂体系配制而成。Veradel Pesu按照最高的行业标准生产，具有独特的性能组合，包括优异的耐磨性、易熔加工性、高纯度和优异的耐化学性。这些特性使其非常适合于运输、电子、化学加工和工业用途。树脂在自然状态下呈黑色。 Veradel® 3300 SL30 is a polyethersulfone (PESU) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and externally lubricated applications. The resin is formulated with a ternary anti-friction/anti-wear additive system comprised of carbon fiber, graphite, and polytetrafluoroethylene (PTFE). Veradel® PESU is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, ease of melt processing, high purity, and excellent chemical resistance. These properties make it well-suited for applications in transportation, electronics, chemical processing, and industrial uses. The resin is black in color in its natural state.	LNP Lubricomp JZL012是一种基于聚醚砜树脂的化合物，含有专有填料PTFE。增加的功能包括：内部润滑。 LNP LUBRICOMP JZL012 is a compound based on Polyethersulfone resin containing Proprietary Filler, PTFE. Added features include: Internally Lubricated.

产品描述
厂家：	比利时索尔维 Solvay	沙特沙伯基础 SABIC
类别：	PES PES	PES PES
填料：	PTFE	PTFE
用途：	工业应用,片材,轴承,棒材,型材,齿轮,汽车领域的应用,衬套
性能特点：	尺寸稳定性好,低摩擦系数,耐高温,耐磨,耐化学性 Good Dimensional Stability,Low coefficient of friction,High Heat Resistance,Good wear resistance,Solvent resistance	润滑性 Lubricating
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Veradel® 3300 SL30 LNP™ LUBRICOMP™ JZL012 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(TD)
Shrinkage rate %

熔体质量流动速率(380℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Veradel® 3300 SL30 LNP™ LUBRICOMP™ JZL012 compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Veradel® 3300 SL30 LNP™ LUBRICOMP™ JZL012 compound 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM E1530

比热容(200°C)
Specific heat capacity J/kg/°C

比热容(50°C)
Specific heat capacity J/kg/°C

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

玻璃化转变温度
Glass transition temperature ℃ ASTM D3418

线性热膨胀系数(流动：0~180℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

机械性能
MECHANICAL Veradel® 3300 SL30 LNP™ LUBRICOMP™ JZL012 compound 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩应力
Compressive stress MPa ISO 604

压缩模量
Compression modulus MPa ISO 604

弯曲应力
Bending stress MPa ISO 178

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应力(屈服)
Tensile stress (yield) MPa ISO 527-2/1A/5

拉伸应变(断裂)
Tensile strain % ISO 527

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

洛氏硬度(M 级)
Rockwell hardness

洛氏硬度(R 级)
Rockwell hardness

加工方式

注射 Veradel® 3300 SL30 LNP™ LUBRICOMP™ JZL012 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 Yield

4 80*10*4

5 80*10*4 mm