技术参数
物理性能 PHYSICAL
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
Color a
Color a
ASTM E313
Color b
Color b
ASTM E313
Color L
Color L
ASTM E313
固有粘度(23℃)
Intrinsic viscosity
密度
Density
g/cm³
ASTM D792
密度(--)
Density
g/cm³
ASTM D1505
密度(--)
Density
g/cm³
ASTM D792
密度(285℃)
Density
g/cm³
ISO 1183/A
表观密度(--)
Apparent density
g/cm³
ASTM D1895
薄膜
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
PPT撕裂阻力(MD:23℃,260.0 µm)
PPT tear resistance
N
ASTM D2582
PPT撕裂阻力(TD:23℃,260.0 µm)
PPT tear resistance
N
ASTM D2582
二氧化碳渗透性(23℃,260.0 µm)
Carbon dioxide permeability
cm³·mm/m²/atm/24 hr
ASTM D1434
割线模量(MD:260 µm)
Secant modulus
MPa
ASTM D882
割线模量(TD:260 µm)
Secant modulus
MPa
ASTM D882
埃尔曼多夫抗撕强度(MD:260 µm)
Elmandorf tear strength
g
ASTM D1922
埃尔曼多夫抗撕强度(TD:260 µm)
Elmandorf tear strength
g
ASTM D1922
抗撕裂蔓延性(MD:23℃,260.0 µm)
Tear resistant vine ductility
kN/m
ASTM D1938
抗撕裂蔓延性(TD:23℃,260.0 µm)
Tear resistant vine ductility
kN/m
ASTM D1938
拉伸应变(MD,屈服,260 µm)
Tensile strain
%
ASTM D882
拉伸应变(MD,断裂,260 µm)
Tensile strain
%
ASTM D882
拉伸应变(TD,屈服,260 µm)
Tensile strain
%
ASTM D882
拉伸应变(TD,断裂,260 µm)
Tensile strain
%
ASTM D882
拉伸强度(MD,屈服,260 µm)
tensile strength
MPa
ASTM D882
拉伸强度(MD,断裂,260 µm)
tensile strength
MPa
ASTM D882
拉伸强度(TD,屈服,260 µm)
tensile strength
MPa
ASTM D882
拉伸强度(TD,断裂,260 µm)
tensile strength
MPa
ASTM D882
水蒸气透过性
Water vapor permeability
g/m²/24 hr
ASTM E96
落锤冲击(-18℃,260 µm)
Drop hammer impact
g
ASTM D1709-A
落锤冲击(23℃,260 µm)
Drop hammer impact
g
ASTM D1709-A
薄膜厚度(测试)
film thickness
µm
裤型撕裂耐性(MD:260 µm)
Pant tear resistance
N/mm
ISO 6383-1
裤型撕裂耐性(TD:260 µm)
Pant tear resistance
N/mm
ISO 6383-1
透氧率(30℃,250 µm,50% RH)
Oxygen permeability
cm³·mm/m²/atm/24 hr
ASTM D3985
冲击性能 IMPACT
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
悬臂梁无缺口冲击强度(-20℃,3.2 mm,注塑成型)
Notched impact strength of cantilever beam
ASTM D4812
悬臂梁无缺口冲击强度(-20℃,注塑成型)
Notched impact strength of cantilever beam
ISO 180/1U
悬臂梁无缺口冲击强度(-30℃,3.2 mm,注塑成型)
Notched impact strength of cantilever beam
ASTM D4812
悬臂梁无缺口冲击强度(-30℃,注塑成型)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(-40℃,3.2 mm,注塑成型)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(-40℃,注塑成型)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
ASTM D4812
悬臂梁无缺口冲击强度(23℃,3.2 mm,注塑成型)
Notched impact strength of cantilever beam
ASTM D4812
悬臂梁无缺口冲击强度(23℃,注塑成型)
Notched impact strength of cantilever beam
ISO 180/1U
悬臂梁缺口冲击强度(-40℃,注塑成型)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-40℃,注塑成型)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃,注塑成型)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃,注塑成型)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
装有测量仪表的落镖冲击(-40℃,2.50 mm,注塑,Energy to Max Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
装有测量仪表的落镖冲击(-40℃,2.50 mm,注塑,能量到力量峰值)
Dart impact equipped with measuring instruments
J
ISO 6603-2
装有测量仪表的落镖冲击(-40℃,3.20 mm,注塑,Energy to Max Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
装有测量仪表的落镖冲击(-40℃,3.20 mm,注塑,能量到力量峰值)
Dart impact equipped with measuring instruments
J
ISO 6603-2
装有测量仪表的落镖冲击(23℃,2.50 mm,注塑,Energy to Max Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
装有测量仪表的落镖冲击(23℃,2.50 mm,注塑,能量到力量峰值)
Dart impact equipped with measuring instruments
J
ISO 6603-2
装有测量仪表的落镖冲击(23℃,3.20 mm,注塑,Energy to Max Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
装有测量仪表的落镖冲击(23℃,3.20 mm,注塑,能量到力量峰值)
Dart impact equipped with measuring instruments
J
ISO 6603-2
装有测量仪表的落镖冲击(23℃,Energy at Peak Load)
Dart impact equipped with measuring instruments
J
ASTM D3763
装有测量仪表的落镖冲击(23℃,Total Energy)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能 THERMAL
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
比热(100℃)
specific heat
J/kg/℃
ASTM C351
比热(200℃)
specific heat
J/kg/℃
ASTM C351
比热(23℃)
specific heat
J/kg/℃
ASTM C351
比热(280℃)
specific heat
J/kg/℃
ASTM C351
比热(80℃)
specific heat
J/kg/℃
ASTM C351
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/B
热变形温度(0.45 MPa,未退火,注塑成型)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/A
热变形温度(1.8 MPa,未退火,注塑)
Hot deformation temperature
℃
ASTM D648
熔融温度
Melting temperature
℃
DSC
玻璃化转变温度
Glass transition temperature
℃
DSC
结晶峰温度(DSC)
Crystallization peak temperature
℃
ASTM D3418
融合热量(23℃)
Fusion heat
kJ/kg
ASTM E793
光学性能 OPTICAL
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
光泽度(60°)
gloss
ASTM D523
光泽度(60°,264 µm)
gloss
ASTM D2457
折射率
Refractive index
透光率(常规,264 µm)
Transmittance
%
ASTM D1003
透光率(总计)
Transmittance
%
ASTM D1003
透光率(总计,264 µm)
Transmittance
%
ASTM D1003
透明度(264 µm)
transparency
ASTM D1746
雾度
Haze
%
ASTM D1003
雾度(264 µm)
Haze
%
ASTM D1003
补充信息
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
颗粒大小
Particle size
mm
颗粒形状
Particle shape
机械性能 MECHANICAL
Eastapak™ 9921
Eastman™ F61HC
单位 UNIT
测试方法 TEST METHOD
弯曲应变(屈服)
Bending strain
%
ASTM D790
弯曲应变(断裂)
Bending strain
%
ASTM D790
弯曲强度(23℃,注塑成型)
bending strength
MPa
ISO 178
弯曲强度(屈服)
bending strength
MPa
ASTM D790
弯曲强度(屈服,23℃,注塑成型)
bending strength
MPa
ASTM D790
弯曲强度(断裂)
bending strength
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ASTM D790
弯曲模量(23℃,注塑成型)
Bending modulus
MPa
ASTM D790
弯曲模量(23℃,注塑成型)
Bending modulus
MPa
ISO 178
拉伸应变(屈服,23℃)
Tensile strain
%
ASTM D638
拉伸应变(断裂,23℃)
Tensile strain
%
ASTM D638
拉伸强度(屈服,23℃)
tensile strength
MPa
ASTM D638
拉伸强度(屈服,23℃,注塑成型)
tensile strength
MPa
ASTM D638
拉伸强度(屈服,23℃,注塑成型)
tensile strength
MPa
ISO 527-2
拉伸强度(断裂,23℃)
tensile strength
MPa
ASTM D638
拉伸强度(断裂,23℃,注塑成型)
tensile strength
MPa
ASTM D638
拉伸强度(断裂,23℃,注塑成型)
tensile strength
MPa
ISO 527-2
拉伸模量(23℃)
Tensile modulus
MPa
ASTM D638
拉伸模量(23℃,注塑成型)
Tensile modulus
MPa
ASTM D638
拉伸模量(23℃,注塑成型)
Tensile modulus
MPa
ISO 527-2
洛氏硬度(R 级,23℃,注塑成型)
Rockwell hardness
ASTM D785