PA6+ABS，TEKAMID™ HT14ST对比PA6+ABS，KOPLA PA6 KRE1010物性表,价格行情_搜料

牌号信息	TEKAMID™ HT14ST 物性表 PA6+ABS & 韩国万都新材指导价格：暂无塑料库存：缺货	KOPLA PA6 KRE1010 物性表 PA6+ABS & 韩国科普拉指导价格：暂无塑料库存：缺货
牌号简介	H14ST是一种无筋PA6/ABS合金产品，具有超强的韧性。 Features H14ST is a unreinforced PA6/ABS alloy product with super toughness. Application Automotive construction, sports and recreation, electrical/electronics Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties.	KOPLA PA6 KRE1010是一种聚酰胺 6 + ABS（尼龙 6+ABS）材料,。该产品在亚太地区有供货,。 KOPLA PA6 KRE1010的主要特性有: 阻燃/额定火焰良好的韧性 KOPLA PA6 KRE1010的典型应用领域为:电气/电子应用 KOPLA PA6 KRE1010 is a Polyamide 6 + ABS (Nylon 6+ABS) material. This product is available in Asia Pacific. Key characteristics of KOPLA PA6 KRE1010 include: Flame retardant/rated flame, Good toughness. A typical application area for KOPLA PA6 KRE1010 is: Electrical/electronics applications.

产品描述
厂家：	韩国万都新材 Mando	韩国科普拉 KOPLA
类别：	PA6+ABS PA 6+ABS	PA6+ABS PA 6+ABS
填料：
用途：	体育用品,电气/电子应用领域,汽车领域的应用	电气元件,车轮,连接器
性能特点：	超高韧性,防火阻燃等级HB Ultra high toughness,HB	韧性好,弯曲性能好,防火阻燃等级HB Good flexibility,High elastic,HB
加工条件：

技术参数

物理性能
PHYSICAL TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water Absorption % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage % ASTM D955

机械性能
MECHANICAL TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ASTM D790

弯曲强度(23℃)
Flexural Strength MPa ASTM D790

弯曲模量
Flexural Modulus MPa ASTM D790

弯曲模量(23℃)
Flexural Modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，3.2mm)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Izod Notched Impact strength ASTM D256

热性能
THERMAL TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
HDT ℃ ASTM D648

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度
Melting temperature ℃

线性热膨胀系数(MD)
Coeff.of linear therm expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame Class Rating UL 94

电气性能
ELECTRICAL TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

加工方式

注射 TEKAMID™ HT14ST KOPLA PA6 KRE1010 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.12 in/min

4 90 kgf-cm/cm

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
备注