PA66，SAXAMID™ 226F3对比PA66，SAXAMID™ 226F3H物性表,价格行情_搜料

牌号信息	SAXAMID™ 226F3 物性表 PA66 & 奥地利SAX 指导价格：暂无塑料库存：缺货	SAXAMID™ 226F3H 物性表 PA66 & 奥地利SAX 指导价格：暂无塑料库存：缺货
牌号简介	SAXAMID™ 226F3是一种聚酰胺6.6注塑级，用15%玻璃纤维加固。该等级适用于加工过程中需要高强度和良好流动性能的应用。 SAXAMID 226F3 is a polyamide 6.6 injection-molding-grade reinforced with 15% glass fibres. This grade is suitable for applications requiring high strength and very good flow properties during processing.	SAXAMID™ 226F3H是一种聚酰胺6.6注塑级，用15%玻璃纤维加固。该等级适用于加工过程中需要高强度和良好流动性能的应用。此外，该等级具有较高含量的热稳定剂，最好在较高的环境温度下使用。 SAXAMID 226F3H is a polyamide 6.6 injection-molding-grade reinforced with 15% glass fibres. This grade is suitable for applications requiring high strength and very good flow properties during processing. Additionally this grade has a higher content of heat stabilizer which is preferred used at higher ambient temperatures.

产品描述
厂家：	奥地利SAX Austria SAX	奥地利SAX Austria SAX
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 15	玻璃纤维 15
用途：
性能特点：	机械强度好,易流动 Good Rigidity,Good liquidity	易流动,机械强度好,热稳定性好 Good liquidity,Good Rigidity,Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SAXAMID™ 226F3 SAXAMID™ 226F3H 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

粘数(H2SO4(硫酸))
Viscosity (H2SO4 (sulfuric acid)) cm³/g ISO 307

机械性能
MECHANICAL SAXAMID™ 226F3 SAXAMID™ 226F3H 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲模量
Flexural Modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT SAXAMID™ 226F3 SAXAMID™ 226F3H 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength kJ/m²

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m²

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m²

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m²

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL SAXAMID™ 226F3 SAXAMID™ 226F3H 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/A

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

加工方式

注射 SAXAMID™ 226F3 SAXAMID™ 226F3H 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 80*10*4mm

2、2.0 mm/min

3、80*10*4 mm