PP，SABIC® PPcompound 9120对比PP，SABIC® PPcompound 7715物性表,价格行情_搜料

牌号信息	SABIC® PPcompound 9120 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货	SABIC® PPcompound 7715 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	SABIC® PPcompound 9120是一种弹性体改性矿物填充聚丙烯，具有优异的冲击和刚度比。典型的材料应用是美观的汽车内饰。它有一个非常高的耐刮性，没有粘性和高流量。SABIC® PPcompound 9120是指定的汽车等级。 SABIC® PPcompound 9120 is an elastomer-modified mineral filled Polypropylene with excellent impact and stiffness ratio. Typical material application are esthetical automotive interior parts. It has a very high scratch resistance, no stickiness and a high flow. SABIC® PPcompound 9120 is a designated automotive grade.	SABIC® PPcompound 7715是一种矿物填充改性聚丙烯。这种材料结合了高耐刮性和高刚度，中等冲击和良好的流动性。该材料具有广阔的加工窗口和良好的物理性能。典型的应用包括美观的汽车内饰，如门板和内饰。SABIC® PPcompound 7715是指定的汽车等级。 SABIC® PPcompound 7715 is a mineral filled modified polypropylene. This material combines high scratch resistance with a high stiffness, medium impact and good flow. This material has a broad processing window combined with good esthical performance. Typical applications include esthetical automotive interior parts such as door panels and interior trim. SABIC® PPcompound 7715 is a designated automotive grade.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PP PP not specified	PP PP not specified
填料：	矿物	矿物
用途：	汽车内部零件,汽车领域的应用	汽车领域的应用,汽车内部装备,汽车内部零件
性能特点：	冲击性能好,流动性高,耐刮擦 High impact resistance,High liquidity,High scratch resistance	机械强度好,冲击性能好,易流动,耐刮擦 Good Rigidity,High impact resistance,Good liquidity,High scratch resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SABIC® PPcompound 9120 SABIC® PPcompound 7715 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(24 hrs)
Shrinkage rate % 内部方法

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT SABIC® PPcompound 9120 SABIC® PPcompound 7715 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃，注塑成型)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(-20℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-4A

悬臂梁缺口冲击强度(0℃，注塑成型)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(0℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-4A

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-4A

简支梁无缺口冲击强度(-40℃，注塑成型)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL SABIC® PPcompound 9120 SABIC® PPcompound 7715 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

线性热膨胀系数(-30 到 30℃)
Linear coefficient of thermal expansion cm/cm/℃

线性热膨胀系数(-30 到 30℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM D696

线性热膨胀系数(23 到 80℃)
Linear coefficient of thermal expansion cm/cm/℃

线性热膨胀系数(23 到 80℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM D696

线性热膨胀系数(MD)
Linear coefficient of thermal expansion ASTM D696

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

机械性能
MECHANICAL SABIC® PPcompound 9120 SABIC® PPcompound 7715 单位
UNIT 测试方法
TEST METHOD

弯曲模量(注塑成型)
Bending modulus MPa ASTM D790

拉伸应变(断裂，3.20 mm，注塑成型)
Tensile strain % ISO 527-2/5/50

拉伸应变(断裂，注塑成型)
Tensile strain % ISO 527-2/1A/50

拉伸强度(屈服，3.20 mm，注塑成型)
tensile strength MPa

拉伸强度(屈服，注塑成型)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(断裂，3.20 mm，注塑成型)
tensile strength MPa

拉伸强度(断裂，注塑成型)
tensile strength MPa ISO 527-2/1A/50

邵氏硬度(邵氏 D，注塑成型)
Shore hardness ISO 868

备注

1 一般属性：这些不能被视为规格。

2 方法 I (三点负荷)

1 一般属性：这些不能被视为规格。

2 方法 I (三点负荷)