牌号信息	Ensinger HYDLAR® Z 物性表 PA66 & 德国恩欣格指导价格：暂无塑料库存：缺货	LUVOCOM® 1-0866 物性表 PA66 & 德国莱曼指导价格：暂无塑料库存：缺货
牌号简介	海德拉有一个物理性能的组合，不能在任何其他商业上可买到的工程塑料。设计工程师利用芳纶纤维增强材料创造了一系列具有优异耐磨性的热塑性塑料。海德拉适用于各种工业应用，其中高强度，极端耐磨性和低磨损是必需的。典型的应用将是耐磨带，轴承，衬套，辊，齿轮和任何地方磨损和耐磨材料的要求。 HYDLAR™ possesses a combination of physical properties that cannot be found in any other commercially available engineered plastic. Design engineers have created a family of superior wear and abrasion resistant thermoplastics using aramid fiber reinforcement. HYDLAR® is applicable to a wide variety of industrial applications where high strength, extreme wear resistance and low abrasiveness are required.Typical applications would be wear strips, bearings, bushings, rollers, gears and wherever wear and abrasion resistant materials are required. High Strength Rods and Plates Extremely Wear Resistant Increased Surface Temperature Capability Highly Resistant to Abrasion No Galling of Mating Wear Surfaces Good Dimensional Stability Outstanding Machinability	LUVOCOM® 1-0866是一种聚酰胺66（尼龙66）材料,含有的填充物为芳族聚酰胺纤维。该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1-0866的主要特性有: 抗翘曲耐热热稳定剂典型应用领域包括: 工程/工业配件纺织/纤维汽车行业商业/办公用品 LUVOCOM® 1-0866是一种聚酰胺66（尼龙66）材料,含有的填充物为芳族聚酰胺纤维。该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 LUVOCOM® 1-0866的主要特性有: 抗翘曲耐热热稳定剂典型应用领域包括: 工程/工业配件纺织/纤维汽车行业商业/办公用品

产品描述
厂家：	德国恩欣格 Ensinger	德国莱曼 Lehmann
类别：	PA66 PA66	PA66 PA66
填料：	有机填料	有机填料
用途：	防磨条,工业应用,齿轮,衬套,轴承,滚轴	汽车领域的应用,工程配件,商务设备,纺织应用,凸轮
性能特点：	机械强度好,尺寸稳定性好,可分散,耐磨 Good Rigidity,Good Dimensional Stability,Machinable,Good wear resistance	低翘曲性,耐高温,热稳定性好 Low warping,High Heat Resistance,Heat Stabilized
加工条件：

技术参数

物理性能
PHYSICAL Ensinger HYDLAR® Z LUVOCOM® 1-0866 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate %

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % DIN 16901

机械性能
MECHANICAL Ensinger HYDLAR® Z LUVOCOM® 1-0866 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲应变
Bending strain % ISO 178

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

磨损因数(1.7 MPa，0.051 m/sec)
Wear factor 10^-8 mm³/N·m ASTM D3702

冲击性能
IMPACT Ensinger HYDLAR® Z LUVOCOM® 1-0866 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1fU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ensinger HYDLAR® Z LUVOCOM® 1-0866 单位
UNIT 测试方法
TEST METHOD

最高使用温度(短期)
Maximum operating temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

连续使用温度
Continuous use temperature ℃

连续使用温度
Continuous use temperature ℃ UL 746B

电气性能
ELECTRICAL Ensinger HYDLAR® Z LUVOCOM® 1-0866 单位
UNIT 测试方法
TEST METHOD

绝缘电阻
insulation resistance ohms IEC 60167

表面电阻率
Surface resistivity ohms IEC 60093

加工方式

注射 Ensinger HYDLAR® Z LUVOCOM® 1-0866 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间

干燥温度

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

热风干燥机, A hr

热风干燥机, A °C

真空干燥机, B hr

真空干燥机, B °C

备注

1 一般属性：这些不能被视为规格。

2 PV=2500

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注