PP，POLYfill PPHC TS25020对比PP，Petrotene® PP A3 T20 HF NTLA010 PH370物性表,价格行情_搜料

牌号信息	POLYfill PPHC TS25020 物性表 PP & 瑞典柏力开米指导价格：暂无塑料库存：缺货	Petrotene® PP A3 T20 HF NTLA010 PH370 物性表 PP & 巴西Petropol 指导价格：暂无塑料库存：缺货
牌号简介	矿物强化 POLYfill PPHC TS25020 is a Polypropylene product filled with 20% mineral. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated.	NYCOA 2062是一种适用于注塑和挤出的尼龙共聚物。这种共聚物具有良好的机械性能和加工性能的平衡。它比标准尼龙树脂熔点低，柔韧性大，结晶度低，是各种挤出应用的理想选择。此外，高相对粘度在NYCOA 2062工艺符合FDA法规21 CFR 177.1500的所有要求后提供了优异的熔融强度和韧性。NYCOA 2062的典型应用包括阻挡膜和管道。 NYCOA 2062 is a Nylon copolymer suitable for injection molding and extrusion. This copolymer offers an excellent balance of mechanical properties and outstanding processability. Its lower melting point, greater flexibility, and lower crystallinity than standard nylon resins, makes it ideal for a variety of extrusion applications. In addition, the high relative viscosity provides excellent melt strength and toughness after process NYCOA 2062 complies with all the requirements of the FDA regulations 21 CFR 177.1500. NYCOA 2062 typical applications include barrier films and tubing.

产品描述
厂家：	瑞典柏力开米 Polykemi	巴西Petropol
类别：	PP PP not specified	PP PP not specified
填料：	矿物 20	矿物 20
用途：
性能特点：	防火阻燃等级HB HB	防火阻燃等级HB HB
加工条件：

技术参数

物理性能
PHYSICAL POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

灰份含量
Ash Content % ASTM D2584

熔体质量流动速率
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度
tensile strength MPa ISO 527-2

冲击性能
IMPACT POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级
Flame retardant level UL 94

电气性能
ELECTRICAL POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 kHz)
Dissipation factor ASTM D150

加工方式

注射 POLYfill PPHC TS25020 Petrotene® PP A3 T20 HF NTLA010 PH370 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 120°C/hr


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
备注
返回顶部

PP，POLYfill PPHC TS25020对比PP，Petrotene® PP A3 T20 HF NTLA010 PH370对比物性表,价格行情_搜料_soliao