PC，Zelux® SD-P对比PC，LNP™ STAT-KON™ DD0009 compound物性表,价格行情_搜料

牌号信息	Zelux® SD-P 物性表 PC & 美国西湖塑料指导价格：暂无塑料库存：缺货	LNP™ STAT-KON™ DD0009 compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Zelux SD-P（静电耗散聚碳酸酯）碳粉填充材料，电阻率水平在1E7-1E11范围内，抗弯强度高，热稳定性好，达到270°F。UL94 V-O额定值为0.030 in，该材料可在0.010“-0.060”仪表上热成型，且具有低排气性能。优点：一致的电阻率值、低出气率、UL 94 V-0防火等级、高强度、易于加工、经久耐用的应用：半导体/电子元件盒式外壳、电信硬件、爆炸物处理设备 ZELUX® SD-P (Static-dissipative Polycarbonate) Carbon-powder-filled material with resistivity levels in the 1E7 - 1E11 range with high flexural strength and good thermal stability to 270° F. UL94 V-O rated at 0.030 in, this material is thermoformable in 0.010" - 0.060" gauges, and has low outgassing properties. Advantages: Consistent resistivity values Low outgassing UL 94 V-0 flame rating High strength Easily machined Durable Applications: Semiconductor/electronic components Cassette housings Telecommunications hardware Explosives handling equipment	LNP™ STAT-KON™ DD0009是基于含碳粉的聚碳酸酯树脂的化合物。这种材料的附加特性包括：导电、阻燃。又称LNP™ STAT-KON™ DD0009产品再订购名称：LNP™ STAT-KON™ DD0009 LNP STAT-KON DD0009 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.

产品描述
厂家：	美国西湖塑料 Westlake Plastics	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	无机填料	无机填料
用途：	电气/电子应用领域,通讯器材,外壳,电气元件
性能特点：	机械强度好,导电,可分散,低VOC,经久耐用,抗静电,热稳定性好,防火阻燃等级V-0 Good Rigidity,Conductive,Machinable,Low odor,Durability,Antistatic property,Heat Stabilized,V-0	导电,阻燃,防火阻燃等级V-0 Conductive,Flame Characteristics,V-0
加工条件：	热成型 Thermo forming	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

冲击性能
IMPACT Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

静电衰减
Electrostatic attenuation sec MIL B-81705

阻燃性能
FLAMMABILITY Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位
UNIT 测试方法
TEST METHOD

0.508 mm
0.508 mm UL 94

1.70 mm
1.70 mm UL 94

机械性能
MECHANICAL Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

加工方式

注射 Zelux® SD-P LNP™ STAT-KON™ DD0009 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
备注