PLA，Ingeo™ 3801X对比PLA，Bio-Flex® A 4100 CL物性表,价格行情_搜料

牌号信息	Ingeo™ 3801X 物性表 PLA & 美国NatureWorks 指导价格：暂无塑料库存：缺货	Bio-Flex® A 4100 CL 物性表 PLA & 德国FKuR 指导价格：暂无塑料库存：缺货
牌号简介	NatureWorks LLC产品Ingeo™ 3801X设计用于需要高热量和高冲击性能的注塑应用。该聚合物级结晶动力学比目前市场上其他的英戈树脂级快得多。快速结晶速度允许在具有高热变形温度的竞争性循环时间下成型结晶部件。Ingeo™ 3801X设计用于注塑应用，其性能要求为热变形温度介于150°F（65°C）和285°F（140°C）之间的不透明注塑件，不需要食品接触批准。 Ingeo 3801X, a NatureWorks LLC product is designed for injection molding applications that require high heat and high impact performance. This polymer grade has much more rapid crystallization kinetics than other Ingeo resin grades currently in the market place. The rapid crystallization rate allows for the molding of crystalline parts at competitive cycle times with high heat distortion temperatures. Ingeo 3801X is designed for injection molding applications where the property requirements are opaque molded parts with heat deflection temperatures between 150°F (65°C) and 285°F (140°C) that do not require food contact approvals.	Bio-Flex® A 4100 CL是一种聚乳酸 (PLA)材料,。该产品在欧洲有供货,加工方式为:薄膜挤出。 Bio-Flex® A 4100 CL的主要特性为:环保/绿色。 Bio-Flex® A 4100 CL的典型应用领域为:电影 Bio-Flex® A 4100 CL is a Polylactic Acid (PLA) material. It is available in Europe for film extrusion. Primary attribute of Bio-Flex® A 4100 CL: Eco-Friendly/Green. Typical application of Bio-Flex® A 4100 CL: Film

产品描述
厂家：	美国NatureWorks	德国FKuR
类别：	PLA PLA	PLA PLA
填料：
用途：		薄膜
性能特点：	冲击性能好,可回收,耐高温 High impact resistance,Renewable resources,High Heat Resistance	可回收,生物可降解,可堆肥 Renewable resources,Biodegradable,Compostable
加工条件：	注射成型 Injection Molding	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL Ingeo™ 3801X Bio-Flex® A 4100 CL 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage % ASTM D955

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

相对粘度
Relative viscosity

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL Ingeo™ 3801X Bio-Flex® A 4100 CL 单位
UNIT 测试方法
TEST METHOD

Tensile Strain at Tensile Strength
Tensile Strain at Tensile Strength % ISO 527

弯曲强度
Flexural Strength MPa ASTM D790

弯曲强度(3.50% 应变)
Flexural Strength MPa ISO 178

弯曲模量
Flexural Modulus MPa ASTM D790

弯曲模量
Flexural Modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(--)
tensile strength MPa ISO 527

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

断裂弯曲应变
Fracture bending strain % ISO 178

冲击性能
IMPACT Ingeo™ 3801X Bio-Flex® A 4100 CL 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Izod Notched Impact strength J/m ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ingeo™ 3801X Bio-Flex® A 4100 CL 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ASTM E2092

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(at 16.5 psi)
HDT ℃ ASTM E2092

熔融温度(DSC)
Melting temperature ℃ ISO 3146

玻璃化转变温度
Glass transition temperature ℃ ASTM D3417

结晶峰温度(DSC)
Crystallization peak temperature ℃ ASTM D3418

维卡软化温度
Vicat Softening Temperature ℃ ISO 306/A

薄膜
Ingeo™ 3801X Bio-Flex® A 4100 CL 单位
UNIT 测试方法
TEST METHOD

氧气传输速率(20 µm)
Oxygen transfer rate cm³/m²/24 hr ISO 15105-2

氮传输速率(25 µm)
Nitrogen transfer rate cm³/m²/24 hr DIN 53380-2

水蒸气透过性
Water vapor permeability g/m²/24 hr ISO 15106-3

加工方式

注射 Ingeo™ 3801X Bio-Flex® A 4100 CL 单位测试方法

加工熔体温度 °C

射嘴温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 20µm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
薄膜
加工方式
注射
备注