牌号信息	Braskem PP PH 0952 物性表 PP均聚 & 巴西布拉斯科指导价格：暂无塑料库存：缺货	Braskem PP H 401 物性表 PP均聚 & 巴西布拉斯科指导价格：暂无塑料库存：缺货
牌号简介	pH0952是一种熔融指数中等的聚丙烯均聚物，含有助滑剂和防堵剂。PH0952是专为铸造和吹塑薄膜挤出工艺膜段和包装而设计的。它具有良好的透明度和光泽度，并且具有很好的加工性能。 PH 0952 is a medium melt flow rate homopolymer, with slip and antiblocking agents. This product is designed for technical films segment and packaging for cast and blown film extrusion. This product features excellent optical properties and good processability. Applications: Coil for automatic packaging; Food and textile packaging; Films for lamination. Processing: Blown Film Extrusion Cast Film Extrusion	H 401是一种中等熔体流动速率的均聚聚丙烯，添加了防滑和防堵剂。专为电影演员设计。该产品具有冲击强度好、透明度和光泽度好、滑动性好、焊接性好等特点。用途：自动包装用线圈；食品和纺织品包装。 H 401 is a medium melt flow rate homopolymer polypropylene, additived with slip and antiblocking agents. Designed specially for cast film. This product features good impact strength, excellent transparency and gloss, good slipping and outstanding weldability. Applications: Coil for automatic packaging; Packages for food and textile products; Packages for retail. Processing: Cast Film Extrusion

产品描述
厂家：	巴西布拉斯科 Braskem	巴西布拉斯科 Braskem
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	薄膜,层压板,流延薄膜,食品包装,纺织应用	食品包装,纺织应用
性能特点：	易加工,透光性好,表面光泽度好,高光滑性,抗结块性,流动性中等,均聚物 Excellent Processability,Good Clarity,Good surface appearance,Smoothness,High anti-blocking,Moderate liquidity,Homopolymer	表面光泽度好,冲击性能好,高光滑性,抗结块性,焊接,均聚物 Good surface appearance,High impact resistance,Smoothness,High anti-blocking,Welding,Homopolymer
加工条件：	流延薄膜	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL Braskem PP PH 0952 Braskem PP H 401 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

薄膜
Braskem PP PH 0952 Braskem PP H 401 单位
UNIT 测试方法
TEST METHOD

割线模量(1% 正割，MD)
Secant modulus MPa ASTM D882

割线模量(1% 正割，MD，吹塑薄膜)
Secant modulus MPa ASTM D882

割线模量(1% 正割，TD)
Secant modulus MPa ASTM D882

割线模量(1% 正割，TD，吹塑薄膜)
Secant modulus MPa ASTM D882

始封温度
Initial sealing temperature ℃

密封起始温度(吹塑薄膜)
Sealing starting temperature (blow molded film) ℃

拉伸应变(MD，屈服)
Tensile strain % ASTM D882

拉伸应变(MD，屈服，吹塑薄膜)
Tensile strain % ASTM D882

拉伸应变(TD，屈服)
Tensile strain % ASTM D882

拉伸应变(TD，屈服，吹塑薄膜)
Tensile strain % ASTM D882

拉伸应变(屈服，注塑成型)
Tensile strain % ASTM D638

拉伸应变(屈服，注塑成型)
Tensile strain % ISO 527-2

拉伸强度(MD，屈服)
tensile strength MPa ASTM D882

拉伸强度(MD，屈服，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服)
tensile strength MPa ASTM D882

拉伸强度(TD，屈服，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(屈服，注塑成型)
tensile strength MPa ASTM D638

拉伸强度(屈服，注塑成型)
tensile strength MPa ISO 527-2

冲击性能
IMPACT Braskem PP PH 0952 Braskem PP H 401 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180

热性能
THERMAL Braskem PP PH 0952 Braskem PP H 401 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，注塑成型)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，注塑)
Hot deformation temperature ℃ ASTM D648

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 3

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

光学性能
OPTICAL Braskem PP PH 0952 Braskem PP H 401 单位
UNIT 测试方法
TEST METHOD

光泽度(45°)
gloss ASTM D2457

光泽度(45°，吹塑薄膜)
gloss ASTM D2457

雾度
Haze % ASTM D1003

雾度(吹塑薄膜)
Haze % ASTM D1003

机械性能
MECHANICAL Braskem PP PH 0952 Braskem PP H 401 单位
UNIT 测试方法
TEST METHOD

弯曲模量(1% 正割，注塑成型)
Bending modulus MPa ASTM D790

弯曲模量(1% 正割，注塑成型)
Bending modulus MPa ISO 178

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

备注

1 一般属性：这些不能被视为规格。

2 压力1 (10N)

1 一般属性：这些不能被视为规格。

2 压力1 (10N)