技术参数
冲击性能 IMPACT
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179
简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
热性能 THERMAL
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
Effective Thermal Diffusivity
Effective Thermal Diffusivity
m²/s
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/B
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/A
熔融温度
Melting temperature
℃
ISO 11357-3
玻璃化转变温度
Glass transition temperature
℃
ISO 11357-2
相对温度指数(0.75 mm)
Relative temperature index
℃
UL 746
相对温度指数(1.5 mm)
Relative temperature index
℃
UL 746
相对温度指数(3.0 mm)
Relative temperature index
℃
UL 746
相对温度指数(冲击机械性能)
Relative temperature index
UL 746
相对温度指数(强度机械性能)
Relative temperature index
UL 746
相对温度指数(电气性能)
Relative temperature index
UL 746
线性热膨胀系数(--)
Linear coefficient of thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数(-40 到 23℃)
Linear coefficient of thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数(55 到 160℃)
Linear coefficient of thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
ISO 11359-2
线性热膨胀系数(MD:23~55℃,2 mm)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD)
Linear coefficient of thermal expansion
ISO 11359-2
线性热膨胀系数(TD:23~55℃,2 mm)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
维卡软化温度(B50)
Vicat Softening Temp
℃
ISO 306
电气性能 ELECTRICAL
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
介电强度
Dielectric strength
kV/mm
IEC 60243-1
介电强度(1 mm)
Dielectric strength
kV/mm
IEC 60243
体积电阻率
Volume resistivity
ohms·cm
IEC 60093
体积电阻率(0.75 mm)
Volume resistivity
ohms·cm
IEC 60093
热丝引燃(0.75 mm)
Hot wire ignition
UL 746
热丝引燃(1.5 mm)
Hot wire ignition
UL 746
热丝引燃(3.0 mm)
Hot wire ignition
UL 746
热丝引燃(HWI)
Hot wire ignition
UL 746
相对电容率(1 MHz)
Relative permittivity
IEC 60250
相对电容率(100 Hz)
Relative permittivity
IEC 60250
相比漏电起痕指数(3.00 mm)
Compared to the leakage tracing index
V
IEC 60112
耐电弧性(3.0 mm)
Arc resistance
ASTM D495
耗散因数(1 MHz)
Dissipation factor
IEC 60250
耗散因数(100 Hz)
Dissipation factor
IEC 60250
表面电阻率
Surface resistivity
ohms
IEC 60093
高电压电弧起痕速率(HVTR)
High voltage arc marking rate
UL 746
高电弧燃烧指数(HAI) (0.75 mm)
High Arc Burning Index (HAI)
UL 746
高电弧燃烧指数(HAI) (1.5 mm)
High Arc Burning Index (HAI)
UL 746
高电弧燃烧指数(HAI) (3.0 mm)
High Arc Burning Index (HAI)
UL 746
阻燃性能 FLAMMABILITY
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
FMVSS 阻燃等级
FMVSS flame retardant rating
FMVSS 302
可燃性等级(0.71 mm)
Flammability level
IEC 60695-11-10, -20
可燃性等级(1.5 mm)
Flammability level
IEC 60695-11-10, -20
极限氧指数
Extreme oxygen index
%
ISO 4589-2
燃烧速率(1 mm)
Burning rate
mm/min
ISO 3795
阻燃等级(0.71 mm)
Flame retardant level
UL 94
阻燃等级(0.75 mm)
Flame retardant level
UL 94
阻燃等级(1.50 mm)
Flame retardant level
UL 94
阻燃等级(3.00 mm)
Flame retardant level
UL 94
机械性能 MECHANICAL
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
Tensile Creep Modulus(1 hr)
Tensile Creep Modulus(1 hr)
MPa
ISO 899-1
弯曲强度
bending strength
MPa
ISO 178
弯曲强度(23℃)
bending strength
MPa
ISO 178
弯曲模量
Bending modulus
MPa
ISO 178
弯曲模量(23℃)
Bending modulus
MPa
ISO 178
拉伸应变(断裂)
Tensile strain
%
ISO 527-2
拉伸应变(断裂,23℃)
Tensile strain
%
ISO 527-2
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2
拉伸强度(断裂,23℃)
tensile strength
MPa
ISO 527-2
拉伸模量
Tensile modulus
MPa
ISO 527-2
拉伸模量(23℃)
Tensile modulus
MPa
ISO 527-2
拉伸蠕变模量(1000 hr)
Tensile creep modulus
MPa
ISO 899-1
泊松比
Poisson's ratio
ISO 527-2
洛氏硬度(M 级)
Rockwell hardness
ISO 2039-2
洛氏硬度(R 级)
Rockwell hardness
ISO 2039-2
物理性能 PHYSICAL
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
Specific Heat Capacity of Melt
Specific Heat Capacity of Melt
J/kg/℃
Thermal Conductivity of Melt
Thermal Conductivity of Melt
W/m/K
吸水率(23℃,24hr)
Water absorption rate
%
ISO 62
吸水率(平衡,23℃,50% RH)
Water absorption rate
%
ISO 62
吸水率(平衡,23℃,50% RH,2.00 mm)
Water absorption rate
%
ISO 62
吸水率(饱和,23℃,2.00 mm)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ISO 1183
收缩率(MD)
Shrinkage rate
%
ISO 294-4
收缩率(MD:23℃,2.0 mm)
Shrinkage rate
%
ISO 294-4
收缩率(TD)
Shrinkage rate
%
ISO 294-4
收缩率(TD:23℃,2.0 mm)
Shrinkage rate
%
ISO 294-4
熔体密度
Melt density
g/cm³
顶出温度
Ejection temperature
℃
补充信息
Zytel® 70G43L NC010
Vydyne® R543
单位 UNIT
测试方法 TEST METHOD
汽车材料(thickness d = 1mm)
Automotive materials
FMVSS 302