PAEK，VICTREX™ WG102对比PAEK，RTP 3883物性表,价格行情_搜料

牌号信息	VICTREX™ WG102 物性表 PAEK & 英国威格斯指导价格：暂无塑料库存：缺货	RTP 3883 物性表 PAEK & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	高性能热塑性材料，聚芳醚酮（PAEK），半结晶，注射成型颗粒，标准流程，用磨损添加剂加固，颜色为黑色。WG102不含聚四氟乙烯（PTFE）或其他卤化添加剂。高温摩擦学应用于高强度和高刚度。耐磨性好，摩擦系数低，热膨胀系数低。抗腐蚀环境的化学反应。 High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, reinforced with wear additives, colour black. WG102 does not contain polytetrafluoroethylene (PTFE) or other halogenated additives. Higher temperature tribological applications for high strength and stiffness. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade.

产品描述
厂家：	英国威格斯 Victrex	美国RTP
类别：	PAEK	PAEK PAEK
填料：
用途：
性能特点：	低摩擦系数,耐化学性,无卤,半结晶,耐磨,机械强度好,易流动 Low coefficient of friction,Solvent resistance,Halogen free,Hypocrystalline,Good wear resistance,Good Rigidity,Good liquidity	机械强度好,易加工,导电,耐化学性,热稳定性好,防火阻燃等级V-0 Good Rigidity,Excellent Processability,Conductive,Solvent resistance,Heat Stabilized,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

冲击性能
IMPACT VICTREX™ WG102 RTP 3883 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度 Izod Unnotched Impact strength(23℃)
Izod Unnotched Impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度 Izod Notched Impact strength(23℃)
Izod Notched Impact strength kJ/m² ISO 180-A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度 Charpy Unnotched Impact strength(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁缺口冲击强度 Charpy notched Impact strength(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL VICTREX™ WG102 RTP 3883 单位
UNIT 测试方法
TEST METHOD

导热系数 Thermal Conductivity(23℃)
Thermal conductivity W/m/K ISO 22007-4

热变形温度 HDT(1.8 MPa，未退火)
Hot deformation temperature HDT ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度 Melting temperature
Melting temperature ℃ ISO 11357-3

玻璃化转变温度 Glass Transition Temperature(--)
Glass Transition Temperature ℃ ISO 11357-2

线性热膨胀系数 Coeff.of linear therm expansion(MD：< 143℃)
Coeff. of linear thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数 Coeff.of linear therm expansion(MD：> 143℃)
Coeff. of linear thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数 Coeff.of linear therm expansion(TD：< 143℃)
Coeff. of linear thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数 Coeff.of linear therm expansion(TD：> 143℃)
Coeff. of linear thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL VICTREX™ WG102 RTP 3883 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率 Volume Resistivity(23℃)
Volume Resistance ohms·cm IEC 60093

机械性能
MECHANICAL VICTREX™ WG102 RTP 3883 单位
UNIT 测试方法
TEST METHOD

压缩强度 Compressive Strength(120℃)
Compressive Strength MPa ISO 604

压缩强度 Compressive Strength(200℃)
Compressive Strength MPa ISO 604

压缩强度 Compressive Strength(23℃)
Compressive Strength MPa ISO 604

压缩强度 Compressive Strength(250℃)
Compressive Strength MPa ISO 604

弯曲强度 Flexural Strength(125℃)
Flexural Strength MPa ISO 178

弯曲强度 Flexural Strength(175℃)
Flexural Strength MPa ISO 178

弯曲强度 Flexural Strength(23℃)
Flexural Strength MPa ISO 178

弯曲强度 Flexural Strength(275℃)
Flexural Strength MPa ISO 178

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量 Flexural Modulus(23℃)
Flexural Modulus MPa ISO 178

拉伸应变 Tensile Strain(断裂 brk，23℃)
Tensile Strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度 Tensile Strength(断裂 brk，125℃)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(断裂 brk，175℃)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(断裂 brk，23℃)
Tensile Strength MPa ISO 527-2

拉伸强度 Tensile Strength(断裂 brk，275℃)
Tensile Strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量 Tensile Modulus(23℃)
Tensile Modulus MPa ISO 527-2

邵氏硬度 Shore hardness(邵氏 D，23℃)
Shore hardness ISO 868

物理性能
PHYSICAL VICTREX™ WG102 RTP 3883 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度 Density
Density g/cm³ ISO 1183

成型收缩率 Molding Shrinkage(MD)
Molding shrinkage % ISO 294-4

成型收缩率 Molding Shrinkage(TD)
Molding shrinkage % ISO 294-4

收缩率(MD)
Shrinkage rate % ASTM D955

螺旋流动长度 spiral flow length(--)
Spiral flow length cm 内部方法

表观粘度 Apparent viscosity(400℃)
Apparent viscosity Pa·s ISO 11443

阻燃性能
FLAMMABILITY VICTREX™ WG102 RTP 3883 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

加工方式

注塑成型 Injection Molding VICTREX™ WG102 RTP 3883 单位测试方法

中段温度 Middle Temperature -Zone 2 °C

前段温度 Front Temperature -Zone 3 °C

后段温度 Rear Temperature -Zone 1 °C

喷嘴温度 Nozzle Temperature °C

干燥时间 Drying Time hr

干燥温度 Drying Temperature °C

料斗温度 Hopper Temperature °C

模具温度 Mold Temperature °C

注射 VICTREX™ WG102 RTP 3883 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 Crystalline

3 模具温度: 374°F, 熔体温度: 770°F

4 1 mm

5 3 mm

6 410°C nozzle, 190°C tool

7 Onset

8 Midpoint

9 Average

10 Along flow

11 1V


相关资讯

牌号简介
产品描述
技术参数
冲击性能
热性能
电气性能
机械性能
物理性能
阻燃性能
加工方式
注塑成型 Injection Molding
注射
备注
返回顶部