HMW-HDPE，LUBMER™ L4640对比HMW-HDPE，TOTAL Polyethylene HDPE XT10 N物性表,价格行情_搜料

牌号信息	LUBMER™ L4640 物性表 HMW-HDPE & 日本三井指导价格：暂无塑料库存：缺货	TOTAL Polyethylene HDPE XT10 N 物性表 HMW-HDPE & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	Lubmer是由Mitusi Chemicals的原始聚合技术开发的一种特殊的聚乙烯。润滑油具有优异的滑动性能、耐磨性和可塑性。尤其是在办公自动化设备、汽车、电气和电子部件的隔音部件上，lubmer被广泛应用。此外，鲁布默还为建筑材料、机械零件等的发展做出了重大贡献。作为一种能创造未来的高性能材料引起人们的关注。特点：滑动性能食品安全耐磨耐化学性电绝缘性能无噪音性能应用：电气/办公自动化设备零件汽车零件通用设备零件建筑材料等零件 LUBMER is a specially polyethylene developed by Mitusi Chemicals' original polymerization technology. LUBMER has outstanding sliding properties, abrasion resistance and moldability. Especially, LUBMER is used for a wide range of applications for soundproofing parts of office automation equipments, automotive, electrical and electronic parts. In addition, LUBMER is making a significant contribution to the development of building materials, mechanical parts, etc.. attracting attention as a high-performance material that will build a future. Features: Sliding properties Food Safety Abrasion resistance Chemical resistance Electrical insulating properties Noiseless properties Applications: Electrical/office automation equipment parts Automotive parts General equipment parts, building materials, and other parts	高分子量双峰管树脂PPI TR4标号PE100/PE4710/PE3408具有优异的高温蠕变断裂强度优异的慢裂纹扩展阻力优异的快速裂纹扩展阻力NSF通过了D2513（气体）、CSA B137.4（气体）、CSA B137.1（水）和CSA C448（地热）NSF标准1的认证。4/61符合FDA认证的气体分配、饮用水、地热、工业和采矿下水道和下水道换衬、天然气和集油、一般管道换衬、管道涂层 High Molecular Weight Bimodal Pipe Resin PPI TR4 designation PE100 / PE4710 / PE3408 Characteristics Outstanding high temperature creep rupture strength Exceptional slow crack growth resistance Excellent resistance to rapid crack propagation NSF certified to D2513 (gas), CSA B137.4 (gas), CSA B137.1 (water) and CSA C448 (geothermal) NSF Standard 14/61 Certified FDA Compliant Applications Gas distribution Potable water Geothermal Industrial and mining Sewer and sewer relining Gas and oil gathering General pipe relining Pipe Coating

产品描述
厂家：	日本三井 Mitsui	法国道达尔 TOTAL
类别：	HMW-HDPE HMW-HDPE	HMW-HDPE HMW-HDPE
填料：
用途：	电气元件,阀门/阀门部件,滚轴,齿轮,机器/机械部件,汽车领域的应用,建筑材料,OA设备,轴承	工业应用,饮用水应用,管道系统,矿业应用,石油/天然气用品,涂层应用
性能特点：	易加工,减震,食品接触,耐磨,耐化学性,绝缘 Excellent Processability,noise reduction,Food contact compliance,Good wear resistance,Solvent resistance,Insulation	高分子量,机械强度好-撕裂,高密度,双峰分子量分布 High molecular weight,Good tear strength,High density,Bimodal molecular weight distribution
加工条件：	注射成型 Injection Molding	管路挤出成型

技术参数

物理性能
PHYSICAL LUBMER™ L4640 TOTAL Polyethylene HDPE XT10 N 单位
UNIT 测试方法
TEST METHOD

PV Limit
PV Limit MPa·m/s 内部方法

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ASTM D792

收缩率(MD：2.0 mm)
Shrinkage rate % 内部方法

收缩率(TD：2.0 mm)
Shrinkage rate % 内部方法

熔体质量流动速率(190℃，10.0kg)
Melt Flow Rate g/10min JIS K7210

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

螺旋流动长度
Spiral flow length cm 内部方法

冲击性能
IMPACT LUBMER™ L4640 TOTAL Polyethylene HDPE XT10 N 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃，2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm，模压成型)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL LUBMER™ L4640 TOTAL Polyethylene HDPE XT10 N 单位
UNIT 测试方法
TEST METHOD

热变形温度
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融峰值温度
Melting peak temperature ℃ ASTM D3417

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 6

脆化温度
Embrittlement temperature ℃ ASTM D746

电气性能
ELECTRICAL LUBMER™ L4640 TOTAL Polyethylene HDPE XT10 N 单位
UNIT 测试方法
TEST METHOD

介电常数(23℃)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 MHz)
Dissipation factor ASTM D150

补充信息
LUBMER™ L4640 TOTAL Polyethylene HDPE XT10 N 单位
UNIT 测试方法
TEST METHOD

Heat Generation Temperature
Heat Generation Temperature ℃ 内部方法

Minimum Required Strength
Minimum Required Strength MPa ISO 9080

Pipe Test Category
Pipe Test Category ASTM D2239

单元分类
Unit classification ASTM D3350

裂纹缓慢扩展 PENT - 模压成型
Slow crack propagation PENT - molding ASTM F1473

机械性能
MECHANICAL LUBMER™ L4640 TOTAL Polyethylene HDPE XT10 N 单位
UNIT 测试方法
TEST METHOD

Notch Pipe Test
Notch Pipe Test day ISO 13479

弯曲强度(23℃，3 mm，48 mm跨度)
bending strength MPa ASTM D790

弯曲模量(23℃，3 mm，48 mm跨距)
Bending modulus MPa ASTM D790

弯曲模量(正割，模压成型)
Bending modulus MPa ASTM D790

抗快速裂缝扩展(Pc，0℃)
Resistance to rapid crack propagation bar ISO 13477

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，模压成型)
Tensile strain % ASTM D638

拉伸强度(屈服，模压成型)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

摩擦系数(动态)
friction coefficient 内部方法

洛氏硬度(R 级)
Rockwell hardness ASTM D785

流体静力学设计基础(23℃)
Fundamentals of Hydrostatic Design MPa

流体静力学设计基础(60℃)
Fundamentals of Hydrostatic Design MPa

磨损量
Wear amount 10^-8 mm³/N·m 内部方法

备注

2 熔体温度: 270°C

3 SUS 304 (surface roughness, 6S)

4 类型 4, 50 mm/min

5 5.0 mm/min

6 压力1 (10N)

1 一般属性：这些不能被视为规格。

2 类型 4, 2.0 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
补充信息
机械性能
加工方式
备注
返回顶部

HMW-HDPE，LUBMER™ L4640对比HMW-HDPE，TOTAL Polyethylene HDPE XT10 N对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别