PA612，LNP™ LUBRICOMP™ IAL12 compound对比PA612，LNP™ LUBRICOMP™ IL004 compound物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ IAL12 compound 物性表 PA612 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ LUBRICOMP™ IL004 compound 物性表 PA612 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LNP Lubricomp_ial12化合物LNPLubricompial12是一种基于尼龙6/12树脂的化合物，含有5%聚四氟乙烯、10%芳纶纤维。这种材料的附加特征是：耐磨。也称为：LNPLubricomp化合物IAL-4012产品再订购名称：IAL12LNP Lubricomp IAL12化合物LNP Lubricomp IAL12是一种基于尼龙6/12树脂的化合物，含有聚四氟乙烯、芳纶纤维。这种材料的附加特性包括：内部润滑。也称为：lnplubricomp化合物IAL-4012产品再订购名称：IAL12 LNP™ LUBRICOMP™ IAL12 compound LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IAL-4012 Product reorder name: IAL12 LNP™ LUBRICOMP™ IAL12 compound LNP LUBRICOMP IAL12 is a compound based on Nylon 6/12 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound IAL-4012 Product reorder name: IAL12	LNP Lubricomp IL004化合物LNP Lubricomp IL004是基于含有20%聚四氟乙烯的尼龙6/12树脂的化合物。这种材料的附加特性包括：耐磨性。也称为：LNPLubricomp化合物IL-4040产品再订购名称：IL004LNP Lubricomp IL004化合物LNP Lubricomp IL004是一种基于尼龙6/12树脂的含有聚四氟乙烯的化合物。这种材料的附加特性包括：内部润滑。也称为：lnplubricomp化合物IL-4040产品再订购名称：IL004 LNP™ LUBRICOMP™ IL004 compound LNP LUBRICOMP IL004 is a compound based on Nylon 6/12 resin containing 20% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IL-4040 Product reorder name: IL004 LNP™ LUBRICOMP™ IL004 compound LNP LUBRICOMP IL004 is a compound based on Nylon 6/12 resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound IL-4040 Product reorder name: IL004

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PA612 PA612	PA612 PA612
填料：	PTFE 5	PTFE 20
用途：
性能特点：	润滑性,耐磨 Lubricating,Good wear resistance	润滑性,耐磨 Lubricating,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ IAL12 compound LNP™ LUBRICOMP™ IL004 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water Absorption % ASTM D570

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage % ASTM D955

收缩率(MD：24 hrs)
Shrinkage % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage % ASTM D955

收缩率(TD：24 hrs)
Shrinkage % ISO 294-4

机械性能
MECHANICAL LNP™ LUBRICOMP™ IAL12 compound LNP™ LUBRICOMP™ IL004 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲模量
Flexural Modulus MPa ASTM D790

弯曲模量
Flexural Modulus MPa ISO 178

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

摩擦系数(动态)
Frictional coefficient ASTM D3702 Modified

摩擦系数(静态)
Frictional coefficient ASTM D3702 Modified

磨损因数(Ring)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

磨损因数(Washer)
Wear factor 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified

冲击性能
IMPACT LNP™ LUBRICOMP™ IAL12 compound LNP™ LUBRICOMP™ IL004 compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multiaxial Impact J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ IAL12 compound LNP™ LUBRICOMP™ IL004 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
HDT ℃ ISO 75-2/Af

加工方式

注射 LNP™ LUBRICOMP™ IAL12 compound LNP™ LUBRICOMP™ IL004 compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 2,0 in/min

3 80*10*4

4 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

PA612，LNP™ LUBRICOMP™ IAL12 compound对比PA612，LNP™ LUBRICOMP™ IL004 compound对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别