PA66，LNP™ THERMOCOMP™ RF00CSXS compound对比PA66，RTP 207.3物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ RF00CSXS compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	RTP 207.3 物性表 PA66 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	LNP Thermocomp RF00CSXS化合物LNP Thermocomp RF00CSXS是一种基于尼龙66树脂的含玻璃纤维化合物。这种材料的附加特性包括：热稳定。又名：lnpThermocomp化合物RF-100-12 hs产品再订购名称：rf00csxs lnp Thermocomp rf00csxs化合物lnpThermocomprf00csxs是一种基于尼龙66树脂的化合物，含有玻璃纤维。这种材料的附加特性包括：热稳定。也称为：lnpThermocomp化合物rf10012hs产品再订购名称：rf00csxs LNP* THERMOCOMP* RF00CSXS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.	此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass fiber reinforced nylon 6/6 offers significant improvements in strength, moduli and deflection temperature over the base polymer. Heat stabilized grade also available.

产品描述
厂家：	沙特沙伯基础 SABIC	美国RTP
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维	玻璃纤维
用途：
性能特点：	热稳定性好 Heat Stabilized	机械强度好,防火阻燃等级HB Good Rigidity,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(--)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

电气性能
ELECTRICAL LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耐电弧性(1.59 mm)
Arc resistance sec ASTM D495

耗散因数(1 MHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注射 LNP™ THERMOCOMP™ RF00CSXS compound RTP 207.3 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.079 in/min

4 Break

5 80*10*4

6 80*10*4 mm

7 2 mm/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注