PA+PP，NEALID NW300 - 8229对比PA+PP，SCHULABLEND® (PA/PP) M/MO 2101 MK10物性表,价格行情_搜料

牌号信息	NEALID NW300 - 8229 物性表 PA+PP & 法国AD Majoris 指导价格：暂无塑料库存：缺货	SCHULABLEND® (PA/PP) M/MO 2101 MK10 物性表 PA+PP & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货
牌号简介	NEALID NW300 - 8229是一种30%的化学耦合矿物增强合金，用于注塑成型。改性后的基础聚丙烯具有良好的工程性能。应用NEALID NW300 - 8229可用于技术要求很高的部件，如：电器部件、电动工具外壳、电气部件、汽车部件、运动和休闲产品。与标准化学耦合矿物聚丙烯化合物相比，NEALID NW300 - 8229的性能得到了改善：具有良好的刚度、耐热性、改善的表面支撑。提高了高温下的抗蠕变性能。 NEALID NW300 - 8229 is a 30 % chemically coupled mineral reinforced alloy intended for injection moulding. The base polypropylene has been modified resulting in high performance engineering properties. APPLICATIONS NEALID NW300 - 8229 can be used for technically demanding components such as: Electrical appliance parts Power tool housings Electrical components Automotive parts Sport and leisure products Improved properties of NEALID NW300 - 8229 compared to standard chemically coupled mineral polypropylene compound: Good stiffness Heat resistance Improved surface properties Increased creep resistance at elevated temperatures	10%填充矿物的PA-PP混合物，具有高耐化学性和低吸水性。 10% mineral filled PA-PP-Blend with high chemical resistance and reduced moisture absorption

产品描述
厂家：	法国AD Majoris	荷兰利安德巴塞尔 LyondellBasell
类别：	PA+PP PA+PP	PA+PP PA+PP
填料：	矿物 30	矿物 10
用途：	家电部件,电气元件,体育用品,汽车领域的应用,外壳
性能特点：	机械强度好,可回收,化学耦合,耐热性好,防火阻燃等级HB Good Rigidity,Renewable resources,Chemical coupling,Heat Resistance, Good,HB	耐化学性,低吸湿性 Solvent resistance,Low moisture absorption
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water Absorption % ISO 62

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

收缩率
Shrinkage %

收缩率(MD)
Shrinkage %

收缩率(TD)
Shrinkage %

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

机械性能
MECHANICAL NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ISO 178

弯曲模量
Flexural Modulus MPa ISO 178

拉伸应力(屈服)
Tensile stress (yield) MPa ISO 527-2/1A/50

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

冲击性能
IMPACT NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/Af

维卡软化温度
Vicat Softening Temperature ℃ ISO 306/B

维卡软化温度
Vicat Softening Temperature ℃ ISO 306/B50

电气性能
ELECTRICAL NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位
UNIT 测试方法
TEST METHOD

介电常数
Dielectric constant DIN 53483

体积电阻率
Volume resistivity ohms·cm DIN 53482

体积电阻率
Volume resistivity ohms·cm IEC 62631-3-1

相比漏电起痕指数
Comparative Tracking Index V DIN 53480

耗散因数(1 kHz)
Dissipation factor DIN 53483

表面电阻率
Surface resistivity ohms DIN 53482

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位
UNIT 测试方法
TEST METHOD

可燃性等级(1.5 mm)
Flammability level

可燃性等级(3.0 mm)
Flammability level

灼热丝可燃性指数(2.0 mm)
Glow Wire Flammability Index(GWFI) ℃ IEC 60695-2-12

燃烧速率(2.0 mm)
Burning Speed mm/min FMVSS 302

燃烧速率(2.0 mm)
Burning Speed mm/min ISO 3795

阻燃等级
Flame Class Rating UL 94

加工方式

注射 NEALID NW300 - 8229 SCHULABLEND® (PA/PP) M/MO 2101 MK10 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部