ABS，Stat-Rite® S-1150对比ABS，LG ABS AF360物性表,价格行情_搜料

牌号信息	Stat-Rite® S-1150 物性表 ABS & 美国路博润指导价格：暂无塑料库存：缺货	LG ABS AF360 物性表 ABS & 韩国LG化学指导价格：暂无塑料库存：缺货
牌号简介	Stat-Rite® S-1150是一种固有耗散聚合物（IDP），采用路博润专利的stat-rite-IDP技术专门开发，与苯乙烯树脂和聚酯树脂一起使用，将永久的静态耗散特性赋予基树脂。Stat-Rite® S-1150与树脂的混合物可以直接注塑或挤压成所需的产品。10-25%的典型负载应使最终产品的表面电阻为10^9-10^11 ohm/平方。具有永久静态耗散湿度独立应用洁净室配件电子设备零件和外壳 Stat-Rite® S-1150 is an Inherently Dissipative Polymer (IDP) specially developed using Lubrizol's patented Stat-Rite® IDP technology for use with styrenic and polyester resins to impart permanent static dissipative property to the base resins. Blends of Stat-Rite® S-1150 with the resins can be directly injection molded or extruded into the desired products. Typical loading of 10-25% shall impart surface resistivities of 10^9 -10^11 ohm/square to the final products. FEATURES Permanently static dissipative Humidity independent APPLICATIONS Cleanroom accessories Electronic equipment parts and housing	LG ABS AF360是一种丙烯腈丁二烯苯乙烯(ABS)材料,。该产品在北美洲、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 LG ABS HI121的主要特性有: 阻燃/额定火焰耐冲击 LG ABS HI121的典型应用领域为:电气/电子应用

产品描述
厂家：	美国路博润 Lubrizol Advanced Materials	韩国LG化学 LG Chemical
类别：	ABS ABS	ABS ABS
填料：
用途：	外壳,电气/电子应用领域,母料,电器外壳,电气元件	电气/电子应用领域
性能特点：	快速静态衰变,抗静电 Rapid Static Decay,Antistatic property	冲击性能好,防火阻燃等级HB High impact resistance,HB
加工条件：	挤出 Extrusion

技术参数

物理性能
PHYSICAL Stat-Rite® S-1150 LG ABS AF360 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Stat-Rite® S-1150 LG ABS AF360 单位
UNIT 测试方法
TEST METHOD

弯曲强度(6.40 mm)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(6.40 mm)
Bending modulus MPa ASTM D790

拉伸应变(屈服，3.20 mm)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服，3.20 mm)
tensile strength MPa ASTM D638

拉伸模量(3.20 mm)
Tensile modulus MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

电气性能
ELECTRICAL Stat-Rite® S-1150 LG ABS AF360 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率(12% RH)
Surface resistivity ohms/sq ESD S11.11

表面电阻(12% R.H.)
Surface resistance ohms ESD S11.11

静电衰减(1000V to 100V，50% R.H.)
Electrostatic attenuation sec CPM

静电衰减(1000V to 10V，50% R.H.)
Electrostatic attenuation sec CPM

冲击性能
IMPACT Stat-Rite® S-1150 LG ABS AF360 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Stat-Rite® S-1150 LG ABS AF360 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525

阻燃性能
FLAMMABILITY Stat-Rite® S-1150 LG ABS AF360 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

加工方式

注射 Stat-Rite® S-1150 LG ABS AF360 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
电气性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注