PP均聚，TIPPLEN® H 388 F对比PP均聚，TOTAL Polypropylene PPH 6088物性表,价格行情_搜料

牌号信息	TIPPLEN® H 388 F 物性表 PP均聚 & 匈牙利MOL 指导价格：暂无塑料库存：缺货	TOTAL Polypropylene PPH 6088 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	TIPPLEN® H 388 F是一种均聚聚丙烯控制的流变性等级，具有高滑脱和抗堵剂含量。该牌号具有良好的加工性、光泽和清晰度。TIPPLEN® H 388 F是专为高速挤出透明铸造和吹塑薄膜而开发的。TIPPLEN® H 388 F建议用于挤压铸造和吹塑的低厚度薄膜，用于食品（如面食、零食、面包制品和糖果）、鲜花、书籍、文具和纺织品的优质包装，可用于0.01-0.15 mm的薄膜。TIPPLEN® H 388 F适用于食品接触。产品符合食品接触法规。 TIPPLEN H 388 F is a homopolymer polypropylene controlled rheology grade with a high slip and antiblock agent content. The grade shows excellent processability, gloss and clarity. TIPPLEN H 388 F is specially developed for high speed extrusion of transparent cast and blown films. TIPPLEN H 388 F is recommended for extrusion of cast and blown low thickness film for quality packaging of foodstuffs (such as pasta, snack, bakery products and confectionary), flowers, books, stationeries and textile goods and it can be used for film from 0.01 - 0.15 mm. TIPPLEN H 388 F is suitable for food contact. The product complies with Food Contact Regulations.	聚丙烯PPH 6088是一种均聚物，其熔体流动指数为9 g/10 min，用于薄膜的挤出成型，具有优异的光学性能和杀菌性能。聚丙烯PPH 6088采用防滑、防堵剂配制而成。建议用于食品包装、纺织品包装、花卉包装、层压膜和文具。 Polypropylene PPH 6088 is a homopolymer with a Melt Flow Index of 9 g/10 min for the cast extrusion of films with excellent optical properties and good sterilizability. Polypropylene PPH 6088 is formulated with slip and anti-block agents. It is recommended for food packaging, textile packaging, flowers packaging, lamination films and stationary supplies.

产品描述
厂家：	匈牙利MOL	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	包装,纺织应用,食品包装,文具,流延薄膜	包装,层压板,流延薄膜,食品包装,文具
性能特点：	易加工,透光性好,表面光泽度好,高光滑性,可回收,抗结块性,食品接触,均聚物 Excellent Processability,Good Clarity,Good surface appearance,Smoothness,Renewable resources,High anti-blocking,Food contact compliance,Homopolymer	高光滑性,易消毒,光学性能,抗结块性,均聚物 Smoothness,Good disinfection,Optical performance,High anti-blocking,Homopolymer
加工条件：	吹塑薄膜	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

冲击性能
IMPACT TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(注塑成型)
Bending modulus MPa ISO 178

拉伸应变(屈服，注塑成型)
Tensile strain % ISO 527-2

拉伸强度(屈服，注塑成型)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(注塑成型)
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

薄膜
TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

埃尔曼多夫抗撕强度(MD：50 µm，铸造薄膜)
Elmandorf tear strength N ISO 6383-2

埃尔曼多夫抗撕强度(TD：50 µm，铸造薄膜)
Elmandorf tear strength N ISO 6383-2

拉伸应变(MD，断裂，50 µm，铸造薄膜)
Tensile strain % ISO 527-3

拉伸应变(TD，断裂，50 µm，铸造薄膜)
Tensile strain % ISO 527-3

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度(MD，屈服，50 µm，吹塑薄膜)
tensile strength MPa ISO 527-3

拉伸强度(TD，屈服，50 µm，吹塑薄膜)
tensile strength MPa ISO 527-3

拉伸强度(屈服)
tensile strength MPa ISO 527-2

落锤冲击(50 µm，铸造薄膜)
Drop hammer impact g ISO 7765-1

薄膜厚度(测试)
film thickness µm

光学性能
OPTICAL TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，50.0 µm，铸造薄膜)
gloss ASTM D2457

雾度(50 µm，铸造薄膜)
Haze % ISO 14782

特殊值
SPECIAL TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

MD，断裂，50 µm，吹塑薄膜
MD, fracture, 50 µ m, blow molded film MPa ISO 527-3

TD，断裂，50 µm，吹塑薄膜
TD, fracture, 50 µ m, blow molded film MPa ISO 527-3

加工方式

挤出 TIPPLEN® H 388 F TOTAL Polypropylene PPH 6088 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

1 SiO2

2 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
薄膜
光学性能
特殊值
加工方式
挤出
备注