技术参数
物理性能 PHYSICAL
LNP™ VERTON™ NV0041EV_GY7E147 compound
LNP™ FARADEX™ NX07344 compound
单位 UNIT
测试方法 TEST METHOD
吸水率(23℃,24hr)
Water absorption rate
%
ISO 62
吸水率(24hr)
Water absorption rate
%
ASTM D570
吸水率(24hr,50% RH)
Water absorption rate
%
ASTM D570
吸水率(平衡,23℃,50% RH)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ASTM D792, ISO 1183
收缩率(MD)
Shrinkage rate
%
收缩率(MD:24 hrs)
Shrinkage rate
%
收缩率(TD)
Shrinkage rate
%
收缩率(TD:24 hrs)
Shrinkage rate
%
机械性能 MECHANICAL
LNP™ VERTON™ NV0041EV_GY7E147 compound
LNP™ FARADEX™ NX07344 compound
单位 UNIT
测试方法 TEST METHOD
弯曲强度(--)
bending strength
MPa
ISO 178
弯曲强度(屈服,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲强度(断裂,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲模量(--)
Bending modulus
MPa
ISO 178
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/5
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/5
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/5
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/5
拉伸模量(--)
Tensile modulus
MPa
ASTM D638
拉伸模量(--)
Tensile modulus
MPa
ISO 527-1-2
断裂弯曲应变
Fracture bending strain
%
ISO 178
冲击性能 IMPACT
LNP™ VERTON™ NV0041EV_GY7E147 compound
LNP™ FARADEX™ NX07344 compound
单位 UNIT
测试方法 TEST METHOD
悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(-40℃)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(-40℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments
J
ISO 6603-2
装有测量仪表的落镖冲击(23℃,Total Energy)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能 THERMAL
LNP™ VERTON™ NV0041EV_GY7E147 compound
LNP™ FARADEX™ NX07344 compound
单位 UNIT
测试方法 TEST METHOD
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Af
线性热膨胀系数(MD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
线性热膨胀系数(MD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(MD:23~60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
线性热膨胀系数(TD:-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(TD:23~60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
维卡软化温度(--)
Vicat Softening Temp
℃
ASTM D1525 16
维卡软化温度(A50)
Vicat Softening Temp
℃
ISO 306/A50
维卡软化温度(B120)
Vicat Softening Temp
℃
ASTM D1525, ISO 306/B120 12 15
阻燃性能 FLAMMABILITY
LNP™ VERTON™ NV0041EV_GY7E147 compound
LNP™ FARADEX™ NX07344 compound
单位 UNIT
测试方法 TEST METHOD
阻燃等级(1.50 mm)
Flame retardant level
UL 94
阻燃等级(1.55 mm)
Flame retardant level
UL 94
电气性能 ELECTRICAL
LNP™ VERTON™ NV0041EV_GY7E147 compound
LNP™ FARADEX™ NX07344 compound
单位 UNIT
测试方法 TEST METHOD
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
屏蔽效力(1.50 mm)
Shielding effectiveness
dB
屏蔽效力(3.00 mm)
Shielding effectiveness
dB
表面电阻率
Surface resistivity
ohms
ASTM D257
静电衰减
Electrostatic attenuation
msec
FTMS 101B