TSU，InnoClear™ OC-7086对比TSU，InnoClear™ OC-7085物性表,价格行情_搜料

牌号信息	InnoClear™ OC-7086 物性表 TSU & 美国Innovative 指导价格：暂无塑料库存：缺货	InnoClear™ OC-7085 物性表 TSU & 美国Innovative 指导价格：暂无塑料库存：缺货
牌号简介	OC-7086是一种水透明的硬质聚氨酯，适用于室温手拌或真空辅助铸造法。无需使用汞、MOCA或TDI，室温固化即可获得优良的物理性能。独特的化学特性使其具有良好的光学清晰度和U.V.保护。混合材料可以铸造成锡或铂硅模具。 OC-7086 is a water-clear, rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. The unique chemistry allows for excellent optical clarity as well as U.V. protection. Mixed material can be cast into either tin or platinum silicone molds.	OC-7085是一种水透明、半刚性聚氨酯，适用于室温手拌或真空辅助铸造法。无需使用汞、MOCA或TDI，室温固化即可获得优异的物理性能。OC-7085独特的化学特性提供了优异的光学清晰度和紫外线稳定性。这种材料专门为锡或铂硅铸模的大批量铸造而制备。 OC-7085 is a water-clear, semi-rigid polyurethane formulated for room temperature hand batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI The unique chemistry of OC-7085 imparts excellent optical clarity as well as UV stability. This material has been specially formulated for mass castings into either tin or platinum silicone molds.

产品描述
厂家：	美国Innovative	美国Innovative
类别：	TSU TSU	TSU TSU
填料：
用途：
性能特点：	机械强度好,耐候抗UV,透光性好 Good Rigidity,Weather resistance is good,Good Clarity	耐候抗UV,透光性好 Weather resistance is good,Good Clarity
加工条件：	真空铸造	真空铸造

技术参数

物理性能
PHYSICAL InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

密度(Hardener)
Density g/cm³

密度(固化处理)
Density g/cm³

密度(基体树脂)
Density g/cm³

收缩率(MD)
Shrinkage rate % ASTM D2566

机械性能
MECHANICAL InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

冲击性能
IMPACT InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

Uncured Properties
InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

固化时间
Curing time hr

粘度(25℃)
viscosity Pa·s

胶凝时间
Gelation time min

Cured Properties
InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

热性能
THERMAL InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热固组件(树脂)
Thermosetting components

热固组件(硬化法)
Thermosetting components

脱模时间
stripping time min

补充信息
InnoClear™ OC-7086 InnoClear™ OC-7085 单位
UNIT 测试方法
TEST METHOD

放热峰值(200g mass)
exothermic peak ℃

备注

1 一般属性：这些不能被视为规格。

2 Resin

3 Mixed

4 Hardener

5 24 hours at 77°F + 4 hours at 150°F

1 一般属性：这些不能被视为规格。

2 Resin

3 Mixed

4 Hardener

5 24 hours at 77°F + 16 hours at 150°F


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
Uncured Properties
Cured Properties
热性能
补充信息
加工方式
备注