牌号信息	HOPELEX PC-1070U 物性表 PC & 韩国乐天指导价格：21971.25元/吨塑料库存： 95750kg	SABIC® PC PC0703R resin 物性表 PC & 沙特沙伯基础指导价格：15697.5元/吨塑料库存： 430500kg
牌号简介	HOPELEX PC-1070U具有较高的粘度、冲击强度、拉伸弯曲强度和弹性模量，可用于板材挤压和严格的要求，如护目镜等。Hopelex PC-1070U具有紫外线稳定成分，可防止最终PC产品在光线下降解。 PC-1070U has higher viscosity, impact strength, tensile & flexural strength, and elastic modulus, which can be used in sheet-extrusion and stringent demand such as and goggles etc. Hopelex PC-1070U have UV stabilized ingredients to prevent degradation of final PC products from lights.	SABIC PC PC0703R树脂PC0703R树脂是一种低流量（300°C/1.2kg时，MFR=7）、热稳定和紫外线稳定的聚碳酸酯产品，具有专为挤出市场设计的脱模剂。仅在www.sabicpc.com上提供 PC0703R resin is a low flow (MFR = 7 at 300°C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the extrusion market. It is available exclusively at www.sabicpc.com

产品描述
厂家：	韩国乐天 LOTTE	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	片材,室外应用
性能特点：	机械强度好,耐候抗UV,冲击性能好,高粘度,拉伸性能好 Good Rigidity,Weather resistance is good,High impact resistance,High Viscosity,Good Tensile Strength	耐候抗UV,流动性低,防火阻燃等级V-2 Weather resistance is good,Low liquidity,V-2
加工条件：	片材挤出成型	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ASTM D4812, ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177, ISO 8302

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(-40 到 95℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(23 到 80℃)
Linear coefficient of thermal expansion cm/cm/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 5

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306/B50, ASTM D1525 15

光学性能
OPTICAL HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542

折射率
Refractive index ASTM D542，ISO 489

透光率
Transmittance % ASTM D1003

透光率(2540 µm)
Transmittance % ASTM D1003

雾度
Haze % ASTM D1003

雾度(2540 µm)
Haze % ASTM D1003

电气性能
ELECTRICAL HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant

介电常数(60 Hz)
Dielectric constant

介电强度(1.6 mm)
Dielectric strength kV/mm ASTM D149，IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257，IEC 60093

耗散因数(1 MHz)
Dissipation factor

耗散因数(60 Hz)
Dissipation factor

阻燃性能
FLAMMABILITY HOPELEX PC-1070U SABIC® PC PC0703R resin 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注射 HOPELEX PC-1070U SABIC® PC PC0703R resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

挤出 HOPELEX PC-1070U SABIC® PC PC0703R resin 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒温度 °C

校准温度，首次 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2,0 in/min

3 0,39 in/min

4 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 2,0 in/min

4 类型 1, 2,0 in/min

5 0,051 in/min

6 0,079 in/min

7 Yield

8 80*10*3

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
光学性能
电气性能
阻燃性能
加工方式
注射
挤出
备注
返回顶部