ABS，Kingfa HC-110对比ABS，Kingfa HR-527物性表,价格行情_搜料

牌号信息	Kingfa HC-110 物性表 ABS & 金发科技指导价格：暂无塑料库存：缺货	Kingfa HR-527 物性表 ABS & 金发科技指导价格：暂无塑料库存：缺货
牌号简介	Kingfa HC-110是一种丙烯腈丁二烯苯乙烯(ABS)材料,。该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa HC-110的主要特性为:阻燃/额定火焰。 Kingfa HC-110的典型应用领域为:汽车行业 Kingfa HC-110 is an acrylonitrile butadiene styrene (ABS) material. This product is available in North America or Asia Pacific and can be processed by injection molding. The main characteristic of Kingfa HC-110 is: Flame retardant/rated flame. A typical application area for Kingfa HC-110 is: Automotive industry.	Kingfa HR-527是一种丙烯腈丁二烯苯乙烯(ABS)材料,。该产品在亚太地区或北美洲有供货,加工方式为:注射成型。 Kingfa HR-527的主要特性有: 阻燃/额定火焰耐冲击 Kingfa HR-527的典型应用领域为:汽车行业 Kingfa HR-527 is an acrylonitrile butadiene styrene (ABS) material. This product is available in Asia Pacific or North America and can be processed by injection molding. Key characteristics of Kingfa HR-527 include: Flame retardant/rated flame, Impact resistant. A typical application area for Kingfa HR-527 is: Automotive industry.

产品描述
厂家：	金发科技 Kingfa	金发科技 Kingfa
类别：	ABS ABS	ABS ABS
填料：
用途：		汽车内部装备,汽车外部零件,汽车内部零件
性能特点：	电镀,防火阻燃等级HB Electroplating,HB	冲击性能好,防火阻燃等级HB High impact resistance,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Kingfa HC-110 Kingfa HR-527 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：23℃)
Shrinkage % ASTM D955

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Kingfa HC-110 Kingfa HR-527 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃，3.2mm)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Izod Notched Impact strength J/m ASTM D256

热性能
THERMAL Kingfa HC-110 Kingfa HR-527 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，6.4 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
HDT ℃ ASTM D648

维卡软化温度(--)
Vicat Softening Temperature ℃ ASTM D1525 3

维卡软化温度(--)
Vicat Softening Temperature ℃ ASTM D1525 4

维卡软化温度(--)
Vicat Softening Temperature ℃ ASTM D1525 5

电气性能
ELECTRICAL Kingfa HC-110 Kingfa HR-527 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

阻燃性能
FLAMMABILITY Kingfa HC-110 Kingfa HR-527 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame Class Rating UL 94

阻燃等级(3.00 mm)
Flame Class Rating UL 94

阻燃等级(3.20 mm)
Flame Class Rating UL 94

机械性能
MECHANICAL Kingfa HC-110 Kingfa HR-527 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ASTM D790

弯曲模量
Flexural Modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

注射 Kingfa HC-110 Kingfa HR-527 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

注射速度 Kingfa HC-110 Kingfa HR-527 单位测试方法

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.079 in/min

4 标准 B (120°C/h), 压力1 (10N)

5 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 2,0 in/min

3 0,079 in/min

4 标准 B (120°C/h), 压力1 (10N)

5 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
注射速度
备注
返回顶部

ABS，Kingfa HC-110对比ABS，Kingfa HR-527对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别