PP均聚，Jampilen HP502N对比PP均聚，TOTAL Polypropylene PPH 7060物性表,价格行情_搜料

牌号信息	Jampilen HP502N 物性表 PP均聚 & 伊朗Jam Polypropylene 指导价格：暂无塑料库存：缺货	TOTAL Polypropylene PPH 7060 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	Jampilen HP502N是一种中等流动性的聚丙烯均聚物，特别适用于生产粗旦短纤维和连续长丝。Jampilen HP502N在挤出过程中表现出良好的工艺稳定性和恒定、高流量。Jampilen HP502N是为纺织地毯、地毯和服装（如工作服和袜子）的羊毛系统纤维而开发的短纤维挤出机。Jampilen HP502N也适用于生产绳索、皮带和皮带的连续长丝。Jampilen HP502N的另一个典型应用是装饰带的挤压。 Jampilen HP502N is a medium fluidity polypropylene homopolymer and is particularly suitable for the production of heavy denier staple fibre and continuous filament. Jampilen HP502N exhibits good process stability and constant, high flow during extrusion. Jampilen HP502N is developed for the extrusion of staple fibres for spinning wool system fibres for carpets, rugs and garments such as overalls and socks. Jampilen HP502N is also suited for the production of continuous filament for ropes, belts and straps. Another typical application of Jampilen HP502N is the extrusion of decorative ribbons.	聚丙烯PPH 7060是一种分子量分布中等、熔体流动指数为12 g/10 min的均聚物，适用于光学性能优异、刚度高的薄膜的挤出成型。聚丙烯PPH 7060适用于包装容器、玩具、家用电器、花园家具和瓶盖的注塑成型。聚丙烯PPH 7060适用于敏感食品包装、标签等应用。 Polypropylene PPH 7060 is a homopolymer with a medium molecular weight distribution and a Melt Flow Index of 12 g/10 min for the cast extrusion of films with excellent optical properties and high stiffness. Polypropylene PPH 7060 is intended for applications like sensitive food packaging, labeling,...

产品描述
厂家：	伊朗Jam Polypropylene	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	细丝,传送带修补,短纤维,绳索,色带,纺织应用,皮带材料,地毯背衬	外壳,食品包装,流延薄膜,标签,玩具,容器,电器用具,家具,护罩
性能特点：	易加工,流动性高,均聚物 Excellent Processability,High liquidity,Homopolymer	机械强度好,光学性能,均聚物 Good Rigidity,Optical performance,Homopolymer
加工条件：	纤维（纺纱）挤出	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

冲击性能
IMPACT Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

加速干燥箱老化(150℃)
Accelerate oven aging hr ASTM D3012

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 1

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

光学性能
OPTICAL Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，50.0 µm，铸造薄膜)
gloss ASTM D2457

光泽度(60°)
gloss ASTM D2457

雾度(50 µm，铸造薄膜)
Haze % ISO 14782

机械性能
MECHANICAL Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

薄膜
Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

埃尔曼多夫抗撕强度(MD：50 µm，铸造薄膜)
Elmandorf tear strength N ISO 6383-2

埃尔曼多夫抗撕强度(TD：50 µm，铸造薄膜)
Elmandorf tear strength N ISO 6383-2

拉伸应变(MD，断裂，50 µm，铸造薄膜)
Tensile strain % ISO 527-3

拉伸应变(TD，断裂，50 µm，铸造薄膜)
Tensile strain % ISO 527-3

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度(MD，屈服，50 µm，吹塑薄膜)
tensile strength MPa ISO 527-3

拉伸强度(TD，屈服，50 µm，吹塑薄膜)
tensile strength MPa ISO 527-3

拉伸强度(屈服)
tensile strength MPa ISO 527-2

落锤冲击(50 µm，铸造薄膜)
Drop hammer impact g ISO 7765-1

薄膜厚度(测试)
film thickness µm

特殊值
SPECIAL Jampilen HP502N TOTAL Polypropylene PPH 7060 单位
UNIT 测试方法
TEST METHOD

MD，断裂，50 µm，吹塑薄膜
MD, fracture, 50 µ m, blow molded film MPa ISO 527-3

TD，断裂，50 µm，吹塑薄膜
TD, fracture, 50 µ m, blow molded film MPa ISO 527-3

备注

1 一般属性：这些不能被视为规格。

2 压力1 (10N)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
光学性能
机械性能
薄膜
特殊值
加工方式
备注
返回顶部

PP均聚，Jampilen HP502N对比PP均聚，TOTAL Polypropylene PPH 7060对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别