PEEK，KetaSpire® KT-820 GF30对比PEEK，SCHULATEC® PEEK GF 30 MV 14物性表,价格行情_搜料

牌号信息	KetaSpire® KT-820 GF30 物性表 PEEK & 比利时索尔维指导价格：暂无塑料库存： 1000kg	SCHULATEC® PEEK GF 30 MV 14 物性表 PEEK & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货
牌号简介	KetaSpire KT- 820 CF30是中等流动性、 30 ％玻纤增强聚醚醚酮（ PEEK）。该树脂的强度和刚度高于未增强KetaSpire PEEK树脂。玻纤增强树脂赋予结构性产品更高的机械强度，特别是工作温度接近300℃时。 KetaSpire PEEK按照最行业最高标准加工，以兼具各种出色的性能为特征，包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。 -米色：KetaSpire KT-820 GF30 BG20 Black: KetaSpire KT-820 GF30 BK95 KetaSpire® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses. Beige: KetaSpire® KT-820 GF30 BG20 Black: KetaSpire KT-820 GF30 BK95	30%玻璃纤维增强聚醚醚酮，中等粘度 30 % glass fiber reinforced polyetheretherketone, medium viscosity

产品描述
厂家：	比利时索尔维 Solvay	荷兰利安德巴塞尔 LyondellBasell
类别：	PEEK PEEK	PEEK
填料：	玻璃纤维 30	玻璃纤维 30
用途：	医疗器材,密封件,飞机应用,牙齿应用领域,医疗器械,工业应用,连接器,医疗/护理用品,电气/电子应用领域,薄膜,石油/天然气用品,外科器械
性能特点：	机械强度好,尺寸稳定性好,易消毒,蒸汽消毒,抗伽马射线,电子束消毒,阻燃,高压灭菌器消毒,耐高温,放射线可穿透,耐疲劳性好,辐射消毒,耐化学性,耐蒸汽,环氧乙烷消毒,加热消毒,防火阻燃等级V-0 Good Rigidity,Good Dimensional Stability,Good disinfection,Steam sterilized,Gamma radiation,E-beam disinfection,Flame Characteristics,High pressure disinfection,High Heat Resistance,Radioactive,Fatigue resistance,Radiation disinfection,Solvent resistance,Resistance to the steam,Ethylene oxide disinfection,Heat sterilization,V-0	防火阻燃等级V-0 V-0
加工条件：	注射成型 Injection Molding	注射成型,挤出 Injection Molding,Extrusion

技术参数

冲击性能
IMPACT KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(--)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(--)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(--)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(--)
Impact strength of cantilever beam notch kJ/m² ISO 180

热性能
THERMAL KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM E1530

比热(200℃)
specific heat J/kg/℃ DSC

比热(50℃)
specific heat J/kg/℃ DSC

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

玻璃化转变温度
Glass transition temperature ℃ ASTM D3418

线性热膨胀系数(MD：-50~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

电气性能
ELECTRICAL KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

介电常数(60 Hz)
Dielectric constant ASTM D150

介电强度(3 mm)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 kHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(60 Hz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位
UNIT 测试方法
TEST METHOD

可燃性等级(0.8 mm)
Flammability level IEC 60695-11-10, -20

可燃性等级(1.6 mm)
Flammability level IEC 60695-11-10, -20

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(20.30 mm)
Flame retardant level UL 94

机械性能
MECHANICAL KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸强度(--)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-2/1A/1

标称拉伸断裂应变(--)
Nominal tensile fracture strain % ASTM D638

标称拉伸断裂应变(--)
Nominal tensile fracture strain % ISO 527-2/1A/5

泊松比
Poisson's ratio ASTM E132

洛氏硬度(M 级)
Rockwell hardness ASTM D785

邵氏硬度(邵氏 D，1 秒)
Shore hardness ASTM D2240

物理性能
PHYSICAL KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD：3.2 mm)
Shrinkage rate % ASTM D955

熔体表观粘度(400℃，1000 sec^-1)
Apparent viscosity of melt Pa·s ASTM D3835

熔体质量流动速率(400℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

加工方式

注射 KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度 KetaSpire® KT-820 GF30 SCHULATEC® PEEK GF 30 MV 14 单位测试方法

螺杆压缩比

备注

1 Passes 60s VB flame, smoke & toxicity requirements.

2 一般属性：这些不能被视为规格。

3 5" x 0.5" x 0.125"

4 0.20 in/min

5 类型1A, 0.20 in/min

1 一般属性：这些不能被视为规格。

2 Measured on annealed samples 3,2 mm thick, 200°C/2h


相关资讯

牌号简介
产品描述
技术参数
冲击性能
热性能
电气性能
阻燃性能
机械性能
物理性能
加工方式
注射
注射速度
备注
返回顶部

PEEK，KetaSpire® KT-820 GF30对比PEEK，SCHULATEC® PEEK GF 30 MV 14对比物性表,价格行情_搜料_soliao