PP均聚，Polifil® PP RMT-20对比PP均聚，TRANSMARE® 10HT20-0.001物性表,价格行情_搜料

牌号信息	Polifil® PP RMT-20 物性表 PP均聚 & 美国TPG 指导价格：暂无塑料库存：缺货	TRANSMARE® 10HT20-0.001 物性表 PP均聚 & 荷兰Transmare 指导价格：暂无塑料库存：缺货
牌号简介	Sylvin 4215-70 Natural是一种乙烯基化合物，由非邻苯二甲酸酯增塑剂配制而成，用于挤出或注射成型应用。 Polifil ® RMT series compounds are high impact polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and high heat deflection resistance. Polifil ® RMT products are UL94 HB rated. These compounds are used in automotive applications and conform to the requirements of the FMVSS-302. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.	TRANSMARE® 10HT20-0.001是一种20%的白色细滑石填充聚丙烯均聚物。它结合了高刚度和良好的流动性能。适合（浅）着色。 TRANSMARE® 10HT20-0.001 is a 20% fine white talc filled polypropylene homopolymer. It combines a high stiffness with good flow properties. Suitable for (light) coloring.

产品描述
厂家：	美国TPG	荷兰Transmare
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	滑石粉 20	滑石粉 20
用途：	工业应用,通用
性能特点：	增塑剂，非DEHP No DEHP plasticizer	机械强度好,可回收,易流动,均聚物 Good Rigidity,Renewable resources,Good liquidity,Homopolymer
加工条件：	挤出 Extrusion	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Polifil® PP RMT-20 TRANSMARE® 10HT20-0.001 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Polifil® PP RMT-20 TRANSMARE® 10HT20-0.001 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(正切，23℃)
Bending modulus MPa ASTM D790

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(屈服，4 mm)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，4 mm)
Tensile strain % ISO 527-2/50

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，4 mm)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂，4 mm)
tensile strength MPa ISO 527-2/50

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

拉伸模量(4 mm)
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 D)
Shore hardness ASTM D1415

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT Polifil® PP RMT-20 TRANSMARE® 10HT20-0.001 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-40℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

落锤冲击(23℃，12.7 mm)
Drop hammer impact J ASTM D3029

热性能
THERMAL Polifil® PP RMT-20 TRANSMARE® 10HT20-0.001 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

加工方式

注射 Polifil® PP RMT-20 TRANSMARE® 10HT20-0.001 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 3-point