PC+ABS，Kingfa JH-R0G30对比PC+ABS，KumhoSunny PC/ABS HAC6030FG物性表,价格行情_搜料

牌号信息	Kingfa JH-R0G30 物性表 PC+ABS & 金发科技指导价格：暂无塑料库存：缺货	KumhoSunny PC/ABS HAC6030FG 物性表 PC+ABS & 上海锦湖日丽指导价格：暂无塑料库存：缺货
牌号简介	Kingfa JH-R0G30是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,含有的填充物为30% 玻璃纤维增强材料。该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa JH-R0G30的主要特性有: 阻燃/额定火焰高刚度加工性能良好 Kingfa JH-R0G30的典型应用领域为:汽车行业 Kingfa JH-R0G30 is a Polycarbonate + ABS (PC+ABS) material filled with 30% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa JH-R0G30 are: Flame Rated Flame Retardant Good Aesthetics Good Dimensional Stability Heat Resistant Typical applications include: Electrical/Electronic Applications Business/Office Goods Engineering/Industrial Parts Housings	HAC630FG是30%GF增强型阻燃PC/ABS树脂，HAC630FG具有较高的阻燃性能和收缩性能，主要用于高耐热性、高稳定测量和阻燃等要求的零件。 HAC6030FG is 30%GF reinforced flame retardan PC/ABS resin.HAC6030FG has high flame retardant properties and shrinking resistance properties.HAC6030FG is mainly used in parts requiring high heat resistance, high stable measurement and flame retardant,etc.

产品描述
厂家：	金发科技 Kingfa	上海锦湖日丽 KumhoSunny
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：	玻璃纤维 30	玻璃纤维 30
用途：	汽车仪表板
性能特点：	机械强度好,易加工,防火阻燃等级V-0 Good Rigidity,Excellent Processability,V-0	阻燃,耐高温,防火阻燃等级V-0,防火阻燃等级5VB Flame Characteristics,High Heat Resistance,V-0,5VB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：23℃)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃，3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

电气性能
ELECTRICAL Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

介电强度(1.6 mm)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm IEC 60093

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(2.00 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

机械性能
MECHANICAL Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

洛氏硬度(M 级)
Rockwell hardness ASTM D785

补充信息
Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位
UNIT 测试方法
TEST METHOD

CSA File No.
CSA File No.

加工方式

注射 Kingfa JH-R0G30 KumhoSunny PC/ABS HAC6030FG 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.39 in/min

3 0.079 in/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
补充信息
加工方式
注射
备注