牌号信息	Polifor® ECO 30 CA/40 GRIGIO Y1 物性表 PP & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	MAJORIS GT420 - 8229 物性表 PP & 法国AD Majoris 指导价格：暂无塑料库存：缺货
牌号简介	聚丙烯，40%矿物填充 W12000138200 - Polypropylene, 40% mineral filled	GT420-8229是一种40%的矿物填充聚丙烯化合物，用于注塑成型。该产品有黑色（GT420-8229）和天然色（GT420）两种颜色，但可根据要求提供其他颜色。GT420-8229流量大，加工性能好。应用GT420-8229已经开发出来，特别是在汽车工业和电气零件的苛刻应用。保险丝盒、连接器盒、各种电器元件、技术用品、要求刚性高、尺寸稳定性高、收缩率低的产品可适当选用GT420-8229制造。 GT420 - 8229 is a 40% mineral filled polypropylene compound intended for injection moulding. The product is available in both black (GT420 - 8229) and natural (GT420) but other colours can be provided on request. GT420 - 8229 has a high flow rate, very good process ability. APPLICATIONS GT420 - 8229 has been developed especially for demanding applications in automotive industry and electrical parts. Fuse and connector boxes Miscellaneous electrical components Technical articles Products requiring rigidity, high dimensional stability, low shrinkage can suitably be made from GT420 - 8229.

产品描述
厂家：	美国塞拉尼斯 Celanese	法国AD Majoris
类别：	PP PP not specified	PP PP not specified
填料：	矿物 40	矿物 40
用途：		汽车领域的应用,电气元件
性能特点：	防火阻燃等级HB HB	机械强度好,易加工,尺寸稳定性好,流动性高,可回收,收缩性低,防火阻燃等级HB Good Rigidity,Excellent Processability,Good Dimensional Stability,High liquidity,Renewable resources,Low contractility,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Polifor® ECO 30 CA/40 GRIGIO Y1 MAJORIS GT420 - 8229 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate %

收缩率
Shrinkage rate % 内部方法

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Polifor® ECO 30 CA/40 GRIGIO Y1 MAJORIS GT420 - 8229 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

冲击性能
IMPACT Polifor® ECO 30 CA/40 GRIGIO Y1 MAJORIS GT420 - 8229 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Polifor® ECO 30 CA/40 GRIGIO Y1 MAJORIS GT420 - 8229 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

阻燃性能
FLAMMABILITY Polifor® ECO 30 CA/40 GRIGIO Y1 MAJORIS GT420 - 8229 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

加工方式

注射 Polifor® ECO 30 CA/40 GRIGIO Y1 MAJORIS GT420 - 8229 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 0.039 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部