COC，TOPAS® 6013F-04对比COC，TOPAS® 9903D-10物性表,价格行情_搜料

牌号信息	TOPAS® 6013F-04 物性表 COC & 日本宝理指导价格：暂无塑料库存：缺货	TOPAS® 9903D-10 物性表 COC & 日本宝理指导价格：暂无塑料库存：缺货
牌号简介	TOPAS 6013F-04是一种高温通用薄膜挤出级。它是一种高透明度无定形树脂，具有高刚度，防潮性，耐化学性，热成型性和食品应用的纯度。它可用于单层和混合浇铸应用，以及铸造和吹塑工艺中的共挤出和共混，适用于需要在耐热泡罩，热灌装和易撕包装等应用中具有出色光学性能的各种薄膜和片材产品。如果不需要在高温下的性能，我们还提供较低的玻璃化转变温度（Tg）等级的TOPAS。包装和薄膜挤出的相关等级 TOPAS 5013F-04 - 高温等级，流量更高 TOPAS® 6013F-04 Product Description TOPAS 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food applications. It is used in monolayer and blended cast applications, and in coextrusions and blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS. Selected Applications Pharmaceutical blisters Decorative film and sheet General packaging Food packaging Food contact Leading Attributes Clarity, forming, barrier, heat resistance, halogen-free Gloss, hardness, chemical resistance, forming Easy or linear tear, heat resistance, hot fill Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 5013F-04 - high temperature grade with higher flow TOPAS® 6013F-04 TOPAS® 6013F-04 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Typical application: Film. Primary characteristic: copolymer.	产品说明TOPAS® 9903D-10是一种非常低的玻璃化转变温度（T g=33°C）薄膜挤出级。它的目的是提供收缩包装应用在低温高收缩。它是一种中等透明度的无定形树脂，具有高硬度、防潮性、耐化学性、热成型性和食品和一般用途的纯度。它用于单层产品中的混合物，单独或多层膜中的混合物。它可用于铸造和吹塑薄膜工艺。主要的薄膜应用是收缩膜和标签。为了提高高温下的性能，建议使用更高的玻璃化转变温度（Tg）等级的TOPA。由于该等级的玻璃化转变温度较低，强烈建议在室温或以下装运和储存球团。选定的应用收缩薄膜和标签食品包装食品接触主要属性低温、低应力、韧性高收缩，不使用双酚A、邻苯二甲酸盐或卤素制造包装和薄膜挤压的广泛法规遵从性相关等级TOPA 9506F-500-坚固低温（T g=65°C）挤压等级TOPAS 9506F-04-高清晰度挤压级 Product Description TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended. Selected Applications Shrink films and labels Food packaging Food contact Leading Attributes High shrink at low temperatures, low stress, toughness Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 9506F-500 - robust low temperature (T g =65°C) extrusion grade

产品描述
厂家：	日本宝理 Polyplastics	日本宝理 Polyplastics
类别：	COC COC	COC COC
填料：
用途：	片材,通用,包装,药品包装,流延薄膜,混合,医疗/护理用品,食品包装	多层薄膜,通用,食品包装,流延薄膜,标签,混合
性能特点：	机械强度好,透光性好,高纯度,表面光泽度好,无卤,食品接触,耐高温,防潮,无BPA,共聚物,耐化学性,无定形的 Good Rigidity,Good Clarity,High purity,Good surface appearance,Halogen free,Food contact compliance,High Heat Resistance,Moisture resistance,No BPA,Copolymer,Solvent resistance,Amorphous	机械强度好,韧性好,高纯度,无卤,食品接触,防潮,无BPA,共聚物,耐化学性,收缩性高,无定形的 Good Rigidity,Good flexibility,High purity,Halogen free,Food contact compliance,Moisture resistance,No BPA,Copolymer,Solvent resistance,High shrinkage,Amorphous
加工条件：	共挤薄膜	吹塑薄膜

技术参数

物理性能
PHYSICAL TOPAS® 6013F-04 TOPAS® 9903D-10 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water Absorption % ISO 62

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ISO 1183

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(230℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(260℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(260℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

热性能
THERMAL TOPAS® 6013F-04 TOPAS® 9903D-10 单位
UNIT 测试方法
TEST METHOD

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2

维卡软化温度
Vicat Softening Temperature

薄膜
TOPAS® 6013F-04 TOPAS® 9903D-10 单位
UNIT 测试方法
TEST METHOD

拉伸应变(MD，断裂，100 µm，铸造薄膜)
Tensile strain % ISO 527-3/50

拉伸应变(TD，断裂，100 µm，铸造薄膜)
Tensile strain % ISO 527-3/50

拉伸强度(MD，断裂，100 µm，吹塑薄膜)
tensile strength MPa ISO 527-3/50

拉伸强度(TD，断裂，100 µm，吹塑薄膜)
tensile strength MPa ISO 527-3/50

拉伸模量(100 µm，铸造薄膜)
Tensile modulus MPa ISO 527-3/1

水气透过率(100 µm，23℃，铸造薄膜，85% RH)
Water vapor transmittance g·mm/m²/atm/24 hr ASTM F1249

薄膜厚度(测试)
film thickness µm

透氧率(23℃，100 µm，挤塑薄膜，50% RH)
Oxygen permeability cm³·mm/m²/atm/24 hr ASTM D3985

光学性能
OPTICAL TOPAS® 6013F-04 TOPAS® 9903D-10 单位
UNIT 测试方法
TEST METHOD

光泽度(60°，100 µm，铸造薄膜)
gloss ISO 2813

雾度(100 µm，铸造薄膜)
Haze % ISO 14782

加工方式

挤出 TOPAS® 6013F-04 TOPAS® 9903D-10 单位测试方法

口模温度 °C

挤塑机进料部分 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

挤出机螺杆长径比L / D TOPAS® 6013F-04 TOPAS® 9903D-10 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 90% RH

3 10°C/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
热性能
薄膜
光学性能
加工方式
挤出
挤出机螺杆长径比L / D
备注
返回顶部