POM共聚，LNP™ LUBRICOMP™ KFL23LH compound对比POM共聚，RTP 805 TFE 15 Z物性表,价格行情_搜料

牌号信息	LNP™ LUBRICOMP™ KFL23LH compound 物性表 POM共聚 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	RTP 805 TFE 15 Z 物性表 POM共聚 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	lnp lubricomp kfl23lh化合物lnp lubricompkfl23lh是一种基于缩醛共聚物树脂的化合物，含有15%玻璃纤维、10%聚四氟乙烯。这种材料的附加特性包括：耐磨、低萃取性。也被称为：LNPLubricomp化合物KFL-4023 LE产品重新订购名称：KFL23HLNP Lubricomp KFL23LH化合物LNP Lubricomp KFL23LH是一种基于乙缩醛共聚物树脂的化合物，含有聚四氟乙烯、玻璃纤维。这种材料的附加特性包括：内部润滑。又名：lnplubricomp化合物KFL-4023 LE产品再订购名称：KFL23LH LNP™ LUBRICOMP™ KFL23LH compound LNP LUBRICOMP KFL23LH is a compound based on Acetal Copolymer resin containing 15% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Low Extractable. Also known as: LNP* LUBRICOMP* Compound KFL-4023 LE Product reorder name: KFL23LH LNP™ LUBRICOMP™ KFL23LH compound LNP LUBRICOMP KFL23LH is a compound based on Acetal Copolymer resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound KFL-4023 LE Product reorder name: KFL23LH	玻璃纤维-聚四氟乙烯润滑-符合FDA的成分 Glass Fiber - PTFE Lubricated - FDA Compliant Ingredients

产品描述
厂家：	沙特沙伯基础 SABIC	美国RTP
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：	PTFE/玻璃纤维 10:15	PTFE/玻璃纤维
用途：
性能特点：	低萃取物,润滑性,耐磨 Low extract,Lubricating,Good wear resistance	润滑性,防火阻燃等级HB Lubricating,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位
UNIT 测试方法
TEST METHOD

含水量
water content %

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate %

机械性能
MECHANICAL LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

阻燃性能
FLAMMABILITY LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

补充信息
LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位
UNIT 测试方法
TEST METHOD

Primary Additive
Primary Additive %

加工方式

注射 LNP™ LUBRICOMP™ KFL23LH compound RTP 805 TFE 15 Z 单位测试方法

Dew Point °C

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

POM共聚，LNP™ LUBRICOMP™ KFL23LH compound对比POM共聚，RTP 805 TFE 15 Z对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别