技术参数
机械性能 MECHANICAL
NORYL™ PVX0800 resin
Hepla® H2018CM EC
单位 UNIT
测试方法 TEST METHOD
Flexural Stress, break(50.0 mm Span, 1.3 mm/min)
Flexural Stress, break
MPa
ASTM D790
Flexural Stress, yield(2.0 mm/min)
Flexural Stress, yield
MPa
ISO 178
Tensile Strain, break, Type I(5.0 mm/min)
Tensile Strain, break, Type I
%
ASTM D638
Tensile Strain, yield, Type I(5.0 mm/min)
Tensile Strain, yield, Type I
%
ASTM D638
Tensile Stress, break, Type I(5.0 mm/min)
Tensile Stress, break, Type I
MPa
ASTM D638
Tensile Stress, yield, Type I(5.0 mm/min)
Tensile Stress, yield, Type I
MPa
ASTM D638
弯曲强度
bending strength
MPa
ISO 178
弯曲强度(屈服,50 mm跨度)
bending strength
MPa
ASTM D790
弯曲强度(屈服,6.40 mm)
bending strength
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ISO 178
弯曲模量(2.0 mm/min)
Bending modulus
MPa
ISO 178
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
弯曲模量(50.0 mm Span, 1.3 mm/min)
Bending modulus
MPa
ASTM D790
弯曲模量(6.40 mm)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/5
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/50
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/5
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/50
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/5
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/50
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/5
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/50
拉伸模量
Tensile modulus
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ISO 527-1-2
拉伸模量
Tensile modulus
MPa
ISO 527-2/1
拉伸模量(5.0 mm/min)
Tensile modulus
MPa
ASTM D638
冲击性能 IMPACT
NORYL™ PVX0800 resin
Hepla® H2018CM EC
单位 UNIT
测试方法 TEST METHOD
Notched Izod Impact, -30℃
Notched Izod Impact, -30℃
J/m
ASTM D256
悬臂梁无缺口冲击强度(80*10*4, -30℃)
Notched impact strength of cantilever beam
kJ/m2
ISO 180/1U
悬臂梁无缺口冲击强度(80*10*4, 23℃)
Notched impact strength of cantilever beam
kJ/m2
ISO 180/1U
悬臂梁缺口冲击强度, 23℃
Impact strength of cantilever beam notch, 23 ℃
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(80*10*4, -30℃)
Impact strength of cantilever beam notch
kJ/m2
ISO 180/1A
悬臂梁缺口冲击强度(80*10*4, 23℃)
Impact strength of cantilever beam notch
kJ/m2
ISO 180/1A
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(80*10*4, 23℃)
Charpy Notched Impact Strength
kJ/m2
ISO 179/1eA
装有测量仪表的落镖冲击(23℃,总能量)
Dart impact equipped with measuring instruments
J
ASTM D3763
飞镖冲击强度(23℃, Total Energy)
Dart impact strength
J
ASTM D3763
热性能 THERMAL
NORYL™ PVX0800 resin
Hepla® H2018CM EC
单位 UNIT
测试方法 TEST METHOD
热变形温度(0.45 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa,未退火,64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Bf
热变形温度(0.45 MPa,未退火,64.0 mm Span, 120*10*4 mm)
Hot deformation temperature
℃
ISO 75-2/Be
热变形温度(0.45MPa,未退火,3.2mm)
Hot deformation temperature
℃
ISO 75-2/Be
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,6.4 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火,64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Af
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(强度机械性能)
Relative temperature index
℃
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
线性热膨胀系数(Flow : 23 to 60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(Transverse : 23 to 60℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525
维卡软化温度
Vicat Softening Temp
℃
ASTM D1525 10
维卡软化温度
Vicat Softening Temp
℃
ISO 306/B120
维卡软化温度
Vicat Softening Temp
℃
ISO 306/B50
电气性能 ELECTRICAL
NORYL™ PVX0800 resin
Hepla® H2018CM EC
单位 UNIT
测试方法 TEST METHOD
体积电阻率
Volume resistivity
ohms·cm
IEC 60093
热丝引燃(HWI)
Hot wire ignition
UL 746
相比漏电起痕指数
Compared to the leakage tracing index
V
IEC 60112
高电弧燃烧指数(HAI)
High Arc Burning Index (HAI)
UL 746
阻燃性能 FLAMMABILITY
NORYL™ PVX0800 resin
Hepla® H2018CM EC
单位 UNIT
测试方法 TEST METHOD
阻燃等级(1.50 mm)
Flame retardant level
UL 94
物理性能 PHYSICAL
NORYL™ PVX0800 resin
Hepla® H2018CM EC
单位 UNIT
测试方法 TEST METHOD
Moisture Absorption(平衡,23℃, 50% RH)
Moisture Absorption
%
ISO 62
吸水率(平衡,23℃,50% RH)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
收缩率(MD:3.20 mm)
Shrinkage rate
%
NFD Method
熔体体积流动速率(220℃,5.0 kg)
Melt Volume Rate
cm3/10min
ISO 1133
熔体体积流动速率(260℃,5 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体体积流动速率(280℃,5 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体表观粘度(280℃,1500 sec^-1)
Apparent viscosity of melt
Pa·s
ISO 11443
熔体质量流动速率(230℃,5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(280℃,5.0 kg)
Melt Flow Rate
g/10 min
ASTM D1238