LDPE，Braskem PE EF2002对比LDPE，Braskem PE TU3001物性表,价格行情_搜料

牌号信息	Braskem PE EF2002 物性表 LDPE & 巴西布拉斯科指导价格：暂无塑料库存：缺货	Braskem PE TU3001 物性表 LDPE & 巴西布拉斯科指导价格：暂无塑料库存：缺货
牌号简介	EF2002是一种高分子量低密度聚乙烯（LDPE）。具有优良的加工性能，适用于高压法生产的支化聚乙烯。EF2002树脂在传统的低密度聚乙烯挤出机中表现出优异的性能，在整个过程中提供低能耗，并允许生产尺寸均匀性好、表面光洁度好的包装。用途：工业包装用高电阻薄膜、重型袋、塑料帆布。大尺寸农用薄膜用基树脂。工艺：吹膜挤出 EF2002 is a low-density polyethylene (LDPE) with high molecular weight. Has excellent processability, proper of branched polyethylene produced by a high-pressure process. EF2002 resin presents an excellent performance in conventional LDPE extruders, granting low energy consumption during the whole process and allowing the production of packaging with a good dimensional uniformity and an excellent surface finishing. Application: High resistance films for industrial packaging, heavy duty bags and plastic canvas. Base resin for agriculture films with big dimensions. Process: Blown Film Extrusion	TU3001是一种低密度聚乙烯（LDPE），具有高分子量、优异的力学性能和良好的加工性能。这些质量保证了薄膜的厚度均匀。TU3001树脂是稳定的受阻胺（HALS）和抗氧化剂，保证高抗老化造成的暴露于太阳辐射。用TU3001制造的薄膜无色，透光率高。生产的薄膜是透明的，但不是热的。根据ASTM D-4976-04A标准规范，本产品为PE 115。用途：温室用胶片。用于需要高机械强度和高抗太阳辐射老化（紫外线辐射）的应用的薄膜。耐用性：使用TU3001制造的薄膜的最小预期持续时间为18个月（两个冬季和一个夏季），可在最大太阳辐射为150 kcal/cm²/年和至少130°的温室中继续使用。M.对于另一个地理区域，请向我们的技术部门寻求帮助。合适的耐久性是指使用纯TU3001生产的薄膜保持至少50%的原始机械阻力。TU3001中使用的紫外线稳定剂对一系列农药具有很强的耐化学性，但含有硫和卤素的化合物会降低薄膜的保质期。 TU3001 is a low-density polyethylene (LDPE) with high molecular weight, excellent mechanical properties and good processability. These qualities ensure the production of films with uniform thickness. TU3001 resin is stabilized with a hindered amine (HALS) and antioxidants which warrants high resistance to aging caused for exposure to solar radiation. Films manufactured with TU3001 are colorless and have high light transmission. The films produced are transparent but not thermal. This product is identified as PE 115 according to ASTM D-4976-04a standard specification. Application: Films for greenhouses. Films for applications that require high mechanical strength and high resistance to aging from solar radiation (UV radiation exposure). Durability: Films manufactured with TU3001 has a minimum duration expectancy of 18 months (two winters and one summer) for continuing use in a greenhouse with a maximum solar radiation of 150 kLy (kcal/cm²/year) and at least 130?m. For another geographic region ask for help in our technical department. The suitable durability refers to the retention of at least 50% of the original mechanical resistance of a film produced with pure TU3001. The UV stabilizer used in TU3001 presents great chemical resistance for a range of pesticides, although compounds which have sulfur and halogens can reduce the films shelf life.

产品描述
厂家：	巴西布拉斯科 Braskem	巴西布拉斯科 Braskem
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	农业应用,包装,重包装袋	薄膜
性能特点：	易加工,表面光泽度好,尺寸稳定性好,高分子量,低密度 Excellent Processability,Good surface appearance,Good Dimensional Stability,High molecular weight,Low density	耐候抗UV,易加工,透光性好,抗氧化,高分子量 Weather resistance is good,Excellent Processability,Good Clarity,Inoxidizability,High molecular weight
加工条件：	吹塑薄膜	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL Braskem PE EF2002 Braskem PE TU3001 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

薄膜
Braskem PE EF2002 Braskem PE TU3001 单位
UNIT 测试方法
TEST METHOD

割线模量(2% 正割，MD：50 µm)
Secant modulus MPa

割线模量(2% 正割，MD：50 µm，吹塑薄膜)
Secant modulus MPa

割线模量(2% 正割，TD：50 µm)
Secant modulus MPa

割线模量(2% 正割，TD：50 µm，吹塑薄膜)
Secant modulus MPa

埃尔曼多夫抗撕强度(MD：150 µm，吹塑薄膜)
Elmandorf tear strength g

埃尔曼多夫抗撕强度(MD：50 µm)
Elmandorf tear strength g

埃尔曼多夫抗撕强度(TD：150 µm，吹塑薄膜)
Elmandorf tear strength g

埃尔曼多夫抗撕强度(TD：50 µm)
Elmandorf tear strength g

拉伸应变(MD，断裂，150 µm，吹塑薄膜)
Tensile strain %

拉伸应变(MD，断裂，50 µm)
Tensile strain %

拉伸应变(TD，断裂，150 µm，吹塑薄膜)
Tensile strain %

拉伸应变(TD，断裂，50 µm)
Tensile strain %

拉伸强度(MD，断裂，150 µm，吹塑薄膜)
tensile strength MPa

拉伸强度(MD，断裂，50 µm)
tensile strength MPa

拉伸强度(TD，断裂，150 µm，吹塑薄膜)
tensile strength MPa

拉伸强度(TD，断裂，50 µm)
tensile strength MPa

落锤冲击(150 µm，吹塑薄膜)
Drop hammer impact g ASTM D1709-B

落锤冲击(50 µm)
Drop hammer impact g ASTM D1709

薄膜厚度(测试)
film thickness µm

光学性能
OPTICAL Braskem PE EF2002 Braskem PE TU3001 单位
UNIT 测试方法
TEST METHOD

光泽度(60°，150 µm，吹塑薄膜)
gloss ASTM D2457

光泽度(60°，50.0 µm)
gloss ASTM D2457

雾度
Haze % ASTM D1003

雾度(150 µm，吹塑薄膜)
Haze % ASTM D1003

补充信息
Braskem PE EF2002 Braskem PE TU3001 单位
UNIT 测试方法
TEST METHOD

UV Stabilizer
UV Stabilizer ppm 内部方法

加工方式

挤出 Braskem PE EF2002 Braskem PE TU3001 单位测试方法

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 F50

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
光学性能
补充信息
加工方式
挤出
备注
返回顶部

LDPE，Braskem PE EF2002对比LDPE，Braskem PE TU3001对比物性表,价格行情_搜料_soliao