PPO(PPE)+PS，SEPAZ™ LW8842FR对比PPO(PPE)+PS，TEKAPPO™ JF201物性表,价格行情_搜料

牌号信息	SEPAZ™ LW8842FR 物性表 PPO(PPE)+PS & 韩国万都新材指导价格：暂无塑料库存：缺货	TEKAPPO™ JF201 物性表 PPO(PPE)+PS & 韩国万都新材指导价格：暂无塑料库存：缺货
牌号简介	SEPAZ™ LW8842FR是一种gf/mf 35%增强改性PPO产品。该产品具有高模量、低翘曲、加工性好等特点。 Features SEPAZ LW8842FR is a GF/MF 35% reinforced modified PPO product. This product has high modulus, low warpage, and good processability. Application DVD ROM tray Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties.	JF201为gf/mf 35%增强型MPPO。JF201具有耐热尺寸稳定性和可燃性V-1 Features JF201 is GF/MF 35% reinforced MPPO. JF201 has heat resistant Dimensional stability Flammability V-1 Application DVD-ROM base tray Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties.

产品描述
厂家：	韩国万都新材 Mando	韩国万都新材 Mando
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：	玻璃纤维/矿物 35	玻璃纤维/矿物 35
用途：
性能特点：	机械强度好,低翘曲性,易加工,防火阻燃等级V-1 Good Rigidity,Low warping,Excellent Processability,V-1	尺寸稳定性好,耐热性好,防火阻燃等级V-1 Good Dimensional Stability,Heat Resistance, Good,V-1
加工条件：

技术参数

物理性能
PHYSICAL SEPAZ™ LW8842FR TEKAPPO™ JF201 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL SEPAZ™ LW8842FR TEKAPPO™ JF201 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

冲击性能
IMPACT SEPAZ™ LW8842FR TEKAPPO™ JF201 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL SEPAZ™ LW8842FR TEKAPPO™ JF201 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

阻燃性能
FLAMMABILITY SEPAZ™ LW8842FR TEKAPPO™ JF201 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

加工方式

注射 SEPAZ™ LW8842FR TEKAPPO™ JF201 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 0.12 in/min

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 0.12 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部

PPO(PPE)+PS，SEPAZ™ LW8842FR对比PPO(PPE)+PS，TEKAPPO™ JF201对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别