PP，SABIC® PPcompound 108CS20对比PP，Advanced Composites ATX639MX2N物性表,价格行情_搜料

牌号信息	SABIC® PPcompound 108CS20 物性表 PP & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Advanced Composites ATX639MX2N 物性表 PP & 美国Advanced Composites 指导价格：暂无塑料库存：缺货
牌号简介	SABIC® PPcompound 108CS20是一种具有良好流动性、冲击性和刚度的材料。该材料是SABICPP CS系统的一部分，也可用作CS系统：使用60%SABICPP 108MF10和40%SABICPP化合物20MBT的混合物可获得如下所示的类似性质。SAbicp化合物108 CS20是指定的汽车等级。 SABIC® PPcompound 108CS20 is a material with good flow, impact and stiffness. The material is part of the SABIC®PP CS systems ans also available as a CS system: using a mixture of 60% SABIC®PP 108MF10 and 40% SABIC®PPcompound 20MBT yields similar properties as listed below. SABIC®PPcompound 108 CS20 is a designated auto grade.	Advanced Composites ATX639MX2N是一种聚丙烯产品,。它,在北美洲有供货。典型应用领域为:汽车行业。特性包括: 耐冲击耐划伤性 Advanced Composites ATX639MX2N is a Polypropylene product. It is available in North America. Typical application: Automotive. Characteristics include: Impact Resistant Scratch Resistant

产品描述
厂家：	沙特沙伯基础 SABIC	美国Advanced Composites
类别：	PP PP not specified	PP PP not specified
填料：
用途：	汽车领域的应用	汽车内部装备
性能特点：	机械强度好,冲击性能好,易流动 Good Rigidity,High impact resistance,Good liquidity	冲击性能好,耐刮擦 High impact resistance,High scratch resistance
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL SABIC® PPcompound 108CS20 Advanced Composites ATX639MX2N 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(24 hrs)
Shrinkage % 内部方法

熔体质量流动速率
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT SABIC® PPcompound 108CS20 Advanced Composites ATX639MX2N 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃，注塑成型)
Izod Notched Impact strength kJ/m² ISO 180-4A

悬臂梁缺口冲击强度(-40℃)
Izod Notched Impact strength kJ/m²

悬臂梁缺口冲击强度(0℃，注塑成型)
Izod Notched Impact strength kJ/m² ISO 180-4A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m²

悬臂梁缺口冲击强度(23℃，注塑成型)
Izod Notched Impact strength ISO 180/4A

简支梁无缺口冲击强度(-40℃，注塑成型)
Charpy Unnotched Impact strength ISO 179/1eU

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength ISO 179/1eA

热性能
THERMAL SABIC® PPcompound 108CS20 Advanced Composites ATX639MX2N 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

线性热膨胀系数(-30 到 30℃)
Coeff.of linear therm expansion cm/cm/℃ ASTM D696

线性热膨胀系数(23 到 80℃)
Coeff.of linear therm expansion cm/cm/℃ ASTM D696

线性热膨胀系数(MD)
Coeff.of linear therm expansion ASTM D696

维卡软化温度
Vicat Softening Temperature ℃ ISO 306/A

机械性能
MECHANICAL SABIC® PPcompound 108CS20 Advanced Composites ATX639MX2N 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Flexural Modulus MPa ISO 178

弯曲模量(注塑成型)
Flexural Modulus MPa ASTM D790

拉伸应变(断裂，3.20 mm，注塑成型)
Tensile strain % ISO 527-2/5/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服，3.20 mm，注塑成型)
tensile strength MPa ISO 527-2/5/50

拉伸强度(断裂，3.20 mm，注塑成型)
tensile strength MPa ISO 527-2/5/50

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，注塑成型)
Shore hardness ISO 868

加工方式

注射 SABIC® PPcompound 108CS20 Advanced Composites ATX639MX2N 单位测试方法

加工熔体温度 °C

垫层 mm

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 方法 I (三点负荷)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
注射
备注
返回顶部