PA66/6，Durethan® BKV 215 H2.0 DUS035 900051对比PA66/6，TECHNYL® A 548B V15 BLACK 23 N物性表,价格行情_搜料

牌号信息	Durethan® BKV 215 H2.0 DUS035 900051 物性表 PA66/6 & 德国朗盛指导价格：暂无塑料库存：缺货	TECHNYL® A 548B V15 BLACK 23 N 物性表 PA66/6 & 德国道默指导价格：暂无塑料库存： 1000kg
牌号简介	Durethan® BKV 215 H2.0 DUS035 900051 含有15%玻璃纤维增强的PA 6共聚物材料，用注射成型的方式加工成型，具有良好的热老化稳定性及良好的抗冲击性能 Durethan® BKV 215 H2.0 DUS035 900051 (干燥 ) PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV 215 H2.0 DUS035 900051 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized	Technyl A 548B V15黑色23 N是一种共聚酰胺6.6/6，用15%的玻璃纤维增强，热稳定，冲击改性，用于吹塑。本产品有黑色可选。 TECHNYL® A 548B V15 Black 23 N is a polyamide 66 reinforced with 15% of glass fibre, heat stabilized, impact modified, for blow moulding. This grade offers an excellent long term Heat resistance and is suitable to work in environments characterized by a very high temperature. It has been also specially designed to be perfectly suitable for blow moulding processing.

产品描述
厂家：	德国朗盛 LANXESS	德国道默 DOMO
类别：	PA66/6 PA66/6	PA66/6 PA66/6
填料：	玻璃纤维 15	玻璃纤维 15
用途：		吹塑成型应用
性能特点：	低翘曲性,冲击性能好,易流动,共聚物,热稳定性好 Low warping,High impact resistance,Good liquidity,Copolymer,Heat Stabilized	耐高温,耐老化,热稳定性好,高粘度,熔体强度好,冲击性能好 High Heat Resistance,Good heat aging resistance,Heat Stabilized,High Viscosity,Good melt strength,High impact resistance
加工条件：	注射成型 Injection Molding	吹塑成型

技术参数

物理性能
PHYSICAL Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

收缩率(MD：120℃，2.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(MD：280℃，2.0 mm)
Shrinkage rate % ISO 2577

收缩率(TD：120℃，2.0 mm，4 hrs)
Shrinkage rate % ISO 2577

收缩率(TD：280℃，2.0 mm)
Shrinkage rate % ISO 2577

表观密度
Apparent density g/cm³ ISO 60

冲击性能
IMPACT Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击能量(-30℃)
Multi axial instrumented impact energy J ISO 6603-2

多轴向仪器化冲击能量(23℃)
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

补充信息
Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 1874

机械性能
MECHANICAL Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain % ISO 178/A

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178-A

弯曲强度(3.50% 应变，23℃)
bending strength MPa ISO 178-A

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/1A

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2/1A

球压硬度
Ball hardness MPa ISO 2039-1

加工方式

注射 Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位测试方法

Residual Moisture Content %

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

挤出 Durethan® BKV 215 H2.0 DUS035 900051 TECHNYL® A 548B V15 BLACK 23 N 单位测试方法

口模温度 °C

建议的最大水分含量 %

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

备注

1 一般属性：这些不能被视为规格。

2 60x60x2mm, 80°C MT, 600 bar

3 60x60x2mm

4 0.079 in/min

5 2 mm/min

6 10°C/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
补充信息
机械性能
加工方式
注射
挤出
备注