PEI，Witcom PEI 6G/3L1对比PEI，ULTEM™ PW2300 resin物性表,价格行情_搜料

牌号信息	Witcom PEI 6G/3L1 物性表 PEI & 荷兰Witcom 指导价格：暂无塑料库存：缺货	ULTEM™ PW2300 resin 物性表 PEI & 沙特沙伯基础指导价格：暂无塑料库存： 3000kg
牌号简介	Witcom PEI 6G/3L1是一种聚醚酰亚胺(PEI)产品,含有的填充物为30% 玻璃纤维增强材料。它可以通过注射成型进行加工,在欧洲有供货。特性包括: 阻燃/额定火焰润滑 Witcom PEI 6G/3L1 is a Polyether Imide (PEI) product filled with 30% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include: Flame Rated Lubricated	ULTEM™ PW2300 resin是一种无定形、不透明、30%玻璃纤维增强的聚醚酰亚胺（PEI）塑料，玻璃化转变温度（Tg）为217°C。这种固有的阻燃树脂经KTW、Wras、ACS、NSF-61和W270认证，并获得美国FDA和欧洲食品接触认证。ULTEM™ PW2300 resin提供特定颜色的设计和认证，用于饮用水应用。 ULTEM PW2300 resin is an amorphous, opaque, 30% glass fiber reinforced polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217?C. This inherently flame retardant resin is KTW, WRAS, ACS, NSF-61 and W270 certified and is US FDA and European Food Contact approved. ULTEM PW2300 resin offers specific colors designed and certified for use in potable water applications.

产品描述
厂家：	荷兰Witcom	沙特沙伯基础 SABIC
类别：	PEI Polyetherimide	PEI Polyetherimide
填料：	玻璃纤维 30	玻璃纤维 30
用途：		饮用水应用
性能特点：	润滑性,防火阻燃等级V-0 Lubricating,V-0	阻燃,食品接触,无定形的 Flame Characteristics,Food contact compliance,Amorphous
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(MD：3.0 mm)
Shrinkage rate % ISO 2577

熔体体积流动速率(360℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

机械性能
MECHANICAL Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ISO 527-1-2

泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber abraser mg 内部方法

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

热性能
THERMAL Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能，3.00 mm)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~150℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~150℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位
UNIT 测试方法
TEST METHOD

0.80 mm
0.80 mm ISO 1210

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

加工方式

注射 Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度 Witcom PEI 6G/3L1 ULTEM™ PW2300 resin 单位测试方法

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 Tensile Bar

3 0.079 in/min

4 Break

5 80*10*4 sp=62mm

6 80*10*4

7 120*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
注射速度
备注
返回顶部