牌号信息	Sinkral® C 333/M2 物性表 ABS & 意大利Versalis 指导价格：暂无塑料库存：缺货	Sinkral® B 532/E 物性表 ABS & 意大利Versalis 指导价格：暂无塑料库存：缺货
牌号简介	特殊的低光泽级注塑成型，结合了中等耐热性和良好的刚度和韧性之间的平衡。名称：热塑性ISO 2580-abs 1，MG，105-04-16-20该等级的主要应用是汽车内饰，例如仪表板仪表和面板，其中亚光表面光洁度和高耐热性是非常理想的。选择这种材料，当在具有适当质量光洁度的工具中进行适当加工时，可能意味着取消后续的喷漆操作，从而降低零件成本，并更容易回收利用。Sinkral® C 333/M2可提供改进的抗紫外线能力（/u）。 Special low gloss grade for injection molding which combines medium heat resistance with a good balance between stiffness and toughness. Designation: Thermoplastic ISO 2580-ABS 1,MG,105-04-16-20 Main application for this grade is automotive interiors, for example dashboard instruments and panels, where a matt surface finish and high thermal resistance are highly desirable. The choice of this material, when properly processed in tools having a suitable quality finish, can mean the elimination of subsequent painting operations with a consequent reduction in part costs together with easier recycling. Sinkral C 333/M2 can be supplied with improved UV resistance (/U).	Sinkral® B 532/E是一个挤压级，结合了高韧性和良好的刚性。大型挤压板的生产要求其流变特性和良好的热稳定性。名称：热塑性塑料ISO 2580-ABS 1，EGN，105-04-25-20大板材，具有良好的表面光洁度（共挤或不共挤，适用于高拉伸比），用于制冷、卫生、汽车、包装和家具（型材）等行业。等级仅适用于自然色。根据要求，该等级的成分可以满足与食品接触的欧洲包装法规。 Sinkral B 532/E is an extrusion grade, which combines high toughness with good rigidity. Its rheological characteristics and good thermal stability are required for the production of large extruded sheet. Designation: Thermoplastics ISO 2580-ABS 1,EGN,105-04-25-20 Large sheet with good surface finish (co-extruded or not and suitable for high draw ratios) for a variety if uses in sectors such as refrigeration, sanitary, automotive, packaging and furniture (profiles). Grade available in natural color only. The composition of this grade, on request, can meet European Regulations for packaging in contact with foodstuffs.

产品描述
厂家：	意大利Versalis	意大利Versalis
类别：	ABS ABS	ABS ABS
填料：
用途：	汽车内部零件	汽车领域的应用,包装,片材,型材,家电部件,卫浴产品,家具
性能特点：	耐候抗UV,耐热性好,刚性韧性平衡,低光泽,防火阻燃等级HB Weather resistance is good,Heat Resistance, Good,Rigid-tough balance,Low Gloss,HB	机械强度好,韧性好,表面光泽度好,热稳定性好,防火阻燃等级HB Good Rigidity,Good flexibility,Good surface appearance,Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	共挤出成型

技术参数

物理性能
PHYSICAL Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % 内部方法

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

悬臂梁缺口冲击强度(0℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

简支梁无缺口冲击强度(-40℃)
Charpy Unnotch Impact strength DIN 53453

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength DIN 53453

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² DIN 53453

热性能
THERMAL Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A120

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

电气性能
ELECTRICAL Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

耗散因数(1 kHz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level Internal Method

阻燃等级(1.50 mm)
Flame retardant level UL 94

补充信息
Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

Designation
Designation

机械性能
MECHANICAL Sinkral® C 333/M2 Sinkral® B 532/E 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

加工方式

注射 Sinkral® C 333/M2 Sinkral® B 532/E 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

挤出 Sinkral® C 333/M2 Sinkral® B 532/E 单位测试方法

干燥时间 hr

干燥温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.079 in/min

4 4 mm

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.079 in/min

4 4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
机械性能
加工方式
注射
挤出
备注