PPO(PPE)+PS，Lumiloy® GN2258FH对比PPO(PPE)+PS，NORYL™ NH7111E resin物性表,价格行情_搜料

牌号信息	Lumiloy® GN2258FH 物性表 PPO(PPE)+PS & 韩国LG化学指导价格：暂无塑料库存：缺货	NORYL™ NH7111E resin 物性表 PPO(PPE)+PS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	注塑等级，阻燃MPPO说明，高强度和高模量，GF增强应用电气和电子零件 Injection Molding Grade, Flame Retardent mPPO Description High Strength & Modulus, GF Reinforced Application Electric and Electronic Parts	noryl nh7111e树脂noryl exnl0280是一种玻璃纤维增强、注塑成型的改性聚苯醚树脂。设计具有良好的尺寸稳定性和低翘曲性，该树脂还使用非卤化FR添加剂，在1.6 mm时达到v1-ul94额定值，在3.00 mm时达到v0-ul94额定值，CTI值为400 V。Noryl Exnl0280可作为要求电绝缘性能、低吸湿性、低翘曲性和低翘曲性的应用的理想材料。d薄壁阻燃。限量浅灰色可选 NORYL™ NH7111E resin NORYL EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR additives to achieve a V1 UL94 rating at 1.6 mm and V0 UL94 at 3.00mm with a CTI value of 400 V. NORYL EXNL0280 may be an excellent material candidate for application requiring electrically insulating properties, low moisture absorption, low warpage and thin wall flame resistance. Available in limited light grey colors

产品描述
厂家：	韩国LG化学 LG Chemical	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS PPO(PPE)+PS	PPO(PPE)+PS PPO(PPE)+PS
填料：	玻璃纤维	玻璃纤维
用途：	电气/电子应用领域	薄壁部件
性能特点：	机械强度好,防火阻燃等级V-0 Good Rigidity,V-0	低翘曲性,尺寸稳定性好,无卤,阻燃,低吸湿性,绝缘,防火阻燃等级V-1,防火阻燃等级V-0 Low warping,Good Dimensional Stability,Halogen free,Flame Characteristics,Low moisture absorption,Insulation,V-1,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Lumiloy® GN2258FH NORYL™ NH7111E resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.0 mm)
Shrinkage rate % ASTM D955

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Lumiloy® GN2258FH NORYL™ NH7111E resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲强度(断裂，3.20 mm)
bending strength MPa ASTM D790

弯曲模量(3.20 mm)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(屈服，3.20 mm)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT Lumiloy® GN2258FH NORYL™ NH7111E resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃，3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Lumiloy® GN2258FH NORYL™ NH7111E resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

阻燃性能
FLAMMABILITY Lumiloy® GN2258FH NORYL™ NH7111E resin 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(2.5 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.00 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

电气性能
ELECTRICAL Lumiloy® GN2258FH NORYL™ NH7111E resin 单位
UNIT 测试方法
TEST METHOD

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

热丝引燃(HWI)
Hot wire ignition UL 746

相对电容率(1 MHz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms IEC 60093

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

加工方式

注射 Lumiloy® GN2258FH NORYL™ NH7111E resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.051 in/min

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
备注
返回顶部

PPO(PPE)+PS，Lumiloy® GN2258FH对比PPO(PPE)+PS，NORYL™ NH7111E resin对比物性表,价格行情_搜料_soliao