PPS，NHU-PPS 1H30C对比PPS，Ryton® QC220N物性表,价格行情_搜料

牌号信息	NHU-PPS 1H30C 物性表 PPS & 浙江新和成指导价格：暂无塑料库存：缺货	Ryton® QC220N 物性表 PPS & 比利时索尔维指导价格：暂无塑料库存：缺货
牌号简介	NHU-PPS聚合物具有分子量分布窄、低聚物含量低、性能稳定等特点。NHU采用先进的自动聚合和后处理技术，生产不同等级的PPS，生产能力在50-3000之间。在NMahile中，NHU可以提供各种规格，包括线性、交联和其他等级。 NHU-PPS 1H30C NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades. NHU-PPS 1H30C NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades.	Ryton PPS纤维级树脂是高分子量聚苯硫醚聚合物，适用于单丝和/或复丝纤维挤出。它们具有优异的热稳定性和耐化学性。 Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and chemical resistance.

产品描述
厂家：	浙江新和成 NHU	比利时索尔维 Solvay
类别：	PPS PPS	PPS PPS
填料：
用途：		纤维
性能特点：	窄分子量分布 Weight distribution	高分子量,耐化学性,热稳定性好 High molecular weight,Solvent resistance,Heat Stabilized
加工条件：	注射成型 Injection Molding	细丝挤出

技术参数

物理性能
PHYSICAL NHU-PPS 1H30C Ryton® QC220N 单位
UNIT 测试方法
TEST METHOD

Chlorine Content
Chlorine Content ppm BS EN 14582

Color L(Hunter)
Color L（Hunter）

吸水率(平衡)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

灰份含量
Ash Content % ISO 3451-1

灰份含量(750℃)
Ash Content % ISO 3451

熔体质量流动速率(316℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(316℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

补充信息
NHU-PPS 1H30C Ryton® QC220N 单位
UNIT 测试方法
TEST METHOD

Volatiles(150℃)
Volatiles（150℃） wt%

加热减量
Heating reduction %

加热减量(300℃)
Heating reduction wt%

挥发性
volatility %

机械性能
MECHANICAL NHU-PPS 1H30C Ryton® QC220N 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

热性能
THERMAL NHU-PPS 1H30C Ryton® QC220N 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD：-50~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

电气性能
ELECTRICAL NHU-PPS 1H30C Ryton® QC220N 单位
UNIT 测试方法
TEST METHOD

介电常数(25 ℃，1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(25℃，1 MHz)
Dissipation factor ASTM D150

加工方式

注射 NHU-PPS 1H30C Ryton® QC220N 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

备注

2 150°C, 1 hour

3 300°C, 1 hour

1 一般属性：这些不能被视为规格。

2 程序 B


相关资讯

牌号简介
产品描述
技术参数
物理性能
补充信息
机械性能
热性能
电气性能
加工方式
注射
备注