PPO(PPE)，NORYL™ NHP5054 resin对比PPO(PPE)，Hepla® H2000物性表,价格行情_搜料

牌号信息	NORYL™ NHP5054 resin 物性表 PPO(PPE) & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Hepla® H2000 物性表 PPO(PPE) & 新孚达指导价格：暂无塑料库存：缺货
牌号简介	NORYL™ NHP5054 resin是一种聚苯醚 (PPE)材料,。该产品在亚太地区有供货,加工方式为:注射成型。 NORYL™ NHP5054 resin的主要特性为:阻燃/额定火焰。 NORYL™ Resin NHP5054 - Asia is a Polyphenylene Ether (PPE) product. It can be processed by injection molding and is available in Asia Pacific. Typical application: Automotive. Primary characteristic: flame rated.	HEPLA®H2000是一种无增强聚苯醚（PPE）产品。其特点包括：符合RoHS标准。一种新的高流量设计，适用于配电箱、继电器箱和接线盒等地下应用。 Hepla® H2000 is a unreinforced Polyphenylene Ether(PPE) product.Characteristics include:RoHS Compliant.A new high flow designed for under-the-hood applications such as power distribution boxes,relay boxes and junction boxes.

产品描述
厂家：	沙特沙伯基础 SABIC	新孚达 NFD
类别：	PPO(PPE) PPO(PPE)	PPO(PPE) PPO(PPE)
填料：
用途：
性能特点：	防火阻燃等级V-0 V-0
加工条件：	注射成型 Injection Molding	Bi-axially Oriented Film

技术参数

物理性能
PHYSICAL NORYL™ NHP5054 resin Hepla® H2000 单位
UNIT 测试方法
TEST METHOD

吸水率(24 hr, 23℃, 50% RH)
Water Absorption % ISO 62

吸水率(24 hr, 23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD： 24 hr)
Shrinkage % ASTM D955

收缩率(TD：24 hr)
Shrinkage % ASTM D955

熔体质量流动速率(250℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(280℃，2.16 kg)
Melt Flow Rate g/10 min ASTM D1238

熔体质量流动速率(280℃，5.0 kg)
Melt Flow Rate g/10 min ASTM D1238

机械性能
MECHANICAL NORYL™ NHP5054 resin Hepla® H2000 单位
UNIT 测试方法
TEST METHOD

Flexural Stress, break
Flexural Stress, break MPa ASTM D790

Tensile Strain, break, Type I(5.0 mm/min)
Tensile Strain, break, Type I % ASTM D638

Tensile Strain, yield, Type I(5.0 mm/min)
Tensile Strain, yield, Type I % ASTM D638

Tensile Stress, break, Type I(5.0 mm/min)
Tensile Stress, break, Type I MPa ASTM D638

Tensile Stress, yield, Type I(5.0 mm/min)
Tensile Stress, yield, Type I MPa ASTM D638

弯曲强度(屈服，100 mm跨度)
Flexural Strength MPa ASTM D790

弯曲强度(屈服，2.0 mm/min)
Flexural Strength MPa ISO 178

弯曲强度(断裂，100 mm Span, 1.3 mm/min)
Flexural Strength

弯曲模量(100 mm Span, 2.6 mm/min)
Flexural Modulus MPa ASTM D790

弯曲模量(100 mm跨距)
Flexural Modulus MPa ASTM D790

弯曲模量(2.0 mm/min)
Flexural Modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸模量(50 mm/min)
Tensile modulus MPa ASTM D638

冲击性能
IMPACT NORYL™ NHP5054 resin Hepla® H2000 单位
UNIT 测试方法
TEST METHOD

Charpy Notched Izod Impact(-20℃)
Charpy Notched Izod Impact kJ/m2 ISO 179/2C

Charpy Notched Izod Impact(23℃)
Charpy Notched Izod Impact kJ/m2 ISO 179/2C

Instrumented Dart Impact, -30℃(Energy at Peak Load)
Instrumented Dart Impact, -30℃ J/m ASTM D3763

Instrumented Dart Impact, 23℃(Energy at Peak Load)
Instrumented Dart Impact, 23℃ J/m ASTM D3763

Notched Izod Impact, -30℃
Notched Izod Impact, -30℃ J/m ASTM D256

悬臂梁缺口冲击强度, 23℃
Impact strength of cantilever beam notch, 23 ℃ J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(80*10*4 , 23℃)
Izod Notched Impact strength kJ/m2 ISO 180/4A

悬臂梁缺口冲击强度(80*10*4 ,-30℃)
Izod Notched Impact strength kJ/m2 ISO 180/4A

热性能
THERMAL NORYL™ NHP5054 resin Hepla® H2000 单位
UNIT 测试方法
TEST METHOD

CLTE - Flow (-40 to 40℃)
CLTE - Flow (-40 to 40℃) 1/℃ ASTM E831

CLTE - Flow (60 to 138℃)
CLTE - Flow (60 to 138℃) 1/℃ ASTM E831

CLTE - Transverse (-40 to 40℃)
CLTE - Transverse (-40 to 40℃) 1/℃ ASTM E831

CLTE - Transverse (60 to 138℃)
CLTE - Transverse (60 to 138℃) 1/℃ ASTM E831

热变形温度(0.45 MPa, Unannealed, 6.40 mm)
HDT ℃ ASTM D648

热变形温度(0.45 MPa，未退火，100 mm Span, 120*10*4 mm)
HDT ℃ ISO 75-2/Be

热变形温度(1.8 MPa，未退火，6.4 mm)
HDT ℃ ASTM D648

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

阻燃性能
FLAMMABILITY NORYL™ NHP5054 resin Hepla® H2000 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame Class Rating UL 94

电气性能
ELECTRICAL NORYL™ NHP5054 resin Hepla® H2000 单位
UNIT 测试方法
TEST METHOD

介电强度(1.60 mm，在油中)
Dielectric strength kV/mm ASTM D149

耗散因数1 MHz
Dissipation factor 1 MHz ASTM D150

加工方式

注射 NORYL™ NHP5054 resin Hepla® H2000 单位测试方法

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

建议注射量 NORYL™ NHP5054 resin Hepla® H2000 单位测试方法

加工熔体温度 °C

射嘴温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 类型 1, 0.20 in/min

3 0.10 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
电气性能
加工方式
注射
建议注射量
备注
返回顶部

PPO(PPE)，NORYL™ NHP5054 resin对比PPO(PPE)，Hepla® H2000对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别