PP共聚，Salflex 613TIC对比PP共聚，PROTEQ™ C35UST23物性表,价格行情_搜料

牌号信息	Salflex 613TIC 物性表 PP共聚 & 加拿大Salflex 指导价格：暂无塑料库存：缺货	PROTEQ™ C35UST23 物性表 PP共聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货
牌号简介	Salflex 613TIC是一种聚丙烯共聚物(PP Copoly)产品,含有的填充物为13% 滑石填料。它可以通过注射成型进行加工,在北美洲有供货。典型应用领域为:汽车行业。 Salflex 613TIC is a Polypropylene Copolymer (PP Copolymer) product filled with 13% talc. It can be processed by injection molding and is available in North America. Typical application: Automotive.	PROTEQ™ C35UST23是一种高熔体流动性的汽车聚丙烯共聚物，含有13%的滑石填料，具有改善热老化和紫外线性能。PROTEQ™ C35UST23的设计符合汽车内饰耐久性规范的严格要求，结合了易加工、低光泽和提高抗磨损性。典型的汽车内饰应用包括控制台、座椅垫、转向罩、车门内衬和杂物箱盖。 PROTEQ™ C35UST23 is one of the higher melt flow automotive polypropylene copolymers which contains 13% talc filler and features improved heat ageing and UV performance. PROTEQ™ C35UST23 has been designed to meet the stringent requirements of automotive interior trim durability specifications, combining easy processing with reduced gloss and improved marr resistance. Typical automotive interior applications are consoles, seat bolsters, steering shrouds, door liners and glovebox lids.

产品描述
厂家：	加拿大Salflex	澳大利亚凯诺斯 Qenos
类别：	PP共聚 PP copolymer	PP共聚 PP copolymer
填料：	滑石粉 13	滑石粉 13
用途：	汽车领域的应用,汽车仪表板,汽车内部装备	汽车内部零件,汽车领域的应用
性能特点：		耐候抗UV,易加工,耐老化,流动性高,共聚物,热稳定性好,低光泽 Weather resistance is good,Excellent Processability,Good heat aging resistance,High liquidity,Copolymer,Heat Stabilized,Low Gloss
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Salflex 613TIC PROTEQ™ C35UST23 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183/A

收缩率
Shrinkage rate % ISO 294-4

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D995

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Salflex 613TIC PROTEQ™ C35UST23 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

冲击性能
IMPACT Salflex 613TIC PROTEQ™ C35UST23 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

热性能
THERMAL Salflex 613TIC PROTEQ™ C35UST23 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY Salflex 613TIC PROTEQ™ C35UST23 单位
UNIT 测试方法
TEST METHOD

灼热丝起燃温度(1.6 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-12

阻燃等级(1.60 mm)
Flame retardant level UL-94

加工方式

注射 Salflex 613TIC PROTEQ™ C35UST23 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2,0 in/min

3 0,051 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部