PC，LEXAN™ OQ3420 resin对比PC，LEXAN™ HP4NR resin物性表,价格行情_搜料

牌号信息	LEXAN™ OQ3420 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ HP4NR resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LEXAN™树脂OQ3420是一种无定形聚碳酸酯树脂。中等粘度，紫外线稳定级别。具有高机械，光学，电气和热性能。提供抗冲击性，出色的尺寸稳定性，优异的透明度和强度。通过注塑加工并用于眼镜镜片。 LEXAN™ resin OQ3420 is an amorphous polycarbonate resin. Medium viscosity, UV stabilized grade. Features high mechanical, optical, electrical, and thermal properties. Offers impact resistance, excellent dimensional stability, excellent transparency and strength. Processed by injection molding and used for ophthalmic lenses.	LEXAN™ HP4NR是一种无定形的聚碳酸酯。具有生物相容性和蒸汽杀菌等级,不包含脱模.中等流动性，良好的延展性，韧性和清晰度。经注射成型加工，用于医疗器械和制药应用。符合ISO10993 / USPVI 等级 LEXAN™ HP4NR is an amorphous polycarbonate. Features biocompatibility and steam sterilizable grade, does not contain mold release. Medium flow, good ductility, toughness, and clarity. Processed by injection molding for medical devices and pharmaceutical applications. Meets ISO10993 / USP Class VI.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	眼镜镜片	制药应用,医疗器械
性能特点：	冲击性能好,尺寸稳定性好 High impact resistance,Good Dimensional Stability	生物兼容性 Biocompatible
加工条件：

技术参数

机械性能
MECHANICAL LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服，1.30 mm/min，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲强度(屈服，2 mm/min)
Flexural Strength MPa ISO 178

弯曲模量(1.30 mm/min，50 mm跨距)
Flexural Modulus MPa ASTM D790

弯曲模量(2 mm/mim)
Flexural Modulus MPa ISO 178

拉伸应变(屈服，50 mm/min)
Tensile strain % ISO 527

拉伸应变(断裂，50 mm/min)
Tensile strain % ISO 527

拉伸强度(屈服，50 mm/min)
tensile strength MPa ISO 527

拉伸强度(屈服，I型，50 mm/min)
tensile strength MPa ASTM D638

拉伸强度(断裂，50 mm/min)
tensile strength MPa ISO 527

拉伸强度(断裂，I型，50 mm/min)
tensile strength MPa ASTM D638

拉伸模量(1 mm/min)
Tensile modulus MPa ISO 527

泰伯磨损(CS-17，1kg)
Taber wear and tear mg/1000cy ASTM D1044

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ASTM D785

纯度(颗粒每克20-50微米)
purity SABIC方法

纯度(颗粒每克> 50微米)
purity SABIC方法

冲击性能
IMPACT LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

仪表冲击总能量(23℃)
Total energy of instrument impact N.m ASTM D 3763

悬臂梁无缺口冲击强度(-30℃，80*10*3)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength J/m ASTM D 4812

悬臂梁无缺口冲击强度(23℃，80*10*3)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，80*10*3)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃，80*10*3)
Izod Notched Impact strength kJ/m² ISO 180-1A

拉伸冲击(S型)
Tensile impact N.m ASTM D 1822

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(80*10*3)
Charpy Notched Impact Strength

落锤冲击(D 3029，23℃)
Gardner Impact N.m ASTM D3029

热性能
THERMAL LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal Conductivity W/m/℃ ASTM C 177

比热
specific heat J/g-℃ ASTM C 351

热变形温度(0.45 MPa)
HDT ℃ ASTM D 648

热变形温度(0.45 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，100 mm跨距)
HDT ℃ ISO 75/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8MPa)
HDT ℃ ASTM D 648

热变形温度(未退火，6.4 mm)
HDT

球压测试(125℃±2℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746B

相对温度指数(电气性能)
Relative temperature index ℃ UL 746B

相对温度指数(非机械冲击性能)
Relative temperature index ℃ UL 746B

线性热膨胀系数(-40℃ 到 95℃，流动)
Coeff.of linear therm expansion 1/℃ ASTM E 831

线性膨胀系数，-40℃ 到 40℃(横向)
Linear expansion coefficient, -40 ℃ to 40 ℃ 1/℃ ASTM E 831

线性膨胀系数，-40℃ 到 40℃(横向)
Linear expansion coefficient, -40 ℃ to 40 ℃ 1/℃ ISO 11359-2

线性膨胀系数，-40℃ 到 40℃(流动)
Linear expansion coefficient, -40 ℃ to 40 ℃ 1/℃ ASTM E 831

线性膨胀系数，-40℃ 到 40℃(流动)
Linear expansion coefficient, -40 ℃ to 40 ℃ 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temperature ℃ ASTM D1525

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

物理性能
PHYSICAL LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，50% RH)
Water Absorption % ISO 62

吸水率(24hr)
Water Absorption % ASTM D570

吸水率(平衡，100℃)
Water Absorption % ASTM D570

吸水率(平衡，23℃)
Water Absorption % ASTM D570

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density ASTM D792

密度
Density ISO 1183

收缩率(MD：3.2 mm)
Shrinkage % 内部方法

比容
Specific volume cm³/g ASTM D 792

熔体体积流动速率(300℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

光学性能
OPTICAL LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542

透光率(2.54 mm)
Light Transmission % ASTM D1003

雾度(2.54 mm)
Haze % ASTM D1003

电气性能
ELECTRICAL LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

介电强度(3.2 mm，在空气中)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

热丝引燃{PLC
Hot wire ignition {PLC PLC Code UL 746A

相对电容率(1 MHz)
Relative permittivity ASTM D150

相对电容率(50-60 Hz)
Relative permittivity ASTM D150

相比漏电起痕指数
Comparative Tracking Index PLC Code UL 746A

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(50-60 Hz)
Dissipation factor ASTM D150

高电压电弧起痕速率 {PLC
High voltage arc marking rate {PLC PLC Code UL 746A

高电流电弧引燃(表面{PLC)
High current arc ignition (surface {PLC) PLC Code UL 746A

阻燃性能
FLAMMABILITY LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位
UNIT 测试方法
TEST METHOD

94HB火焰等级评定
94HB flame rating assessment mm UL 94

极限氧指数(LOI)
Oxygen Index % ASTM D2863

加工方式

注塑成型 LEXAN™ OQ3420 resin LEXAN™ HP4NR resin 单位测试方法

中段2区温度 °C

前段3区温度 °C

后段1区温度 °C

喷嘴温度 °C

射到气缸尺寸 %

干燥时间 hrs

干燥时间累计 hrs

干燥温度

干燥温度 °C

排气槽深度 mm

最大含水量 %

模温 °C

熔体温度 °C

背压 MPa

螺杆转速 rpm

备注


相关资讯

牌号简介
产品描述
技术参数
机械性能
冲击性能
热性能
物理性能
光学性能
电气性能
阻燃性能
加工方式
注塑成型
备注