PC+ABS，LEXAN™ HPS6S resin对比PC+ABS，ASTALOY™ PC/ABS EHA物性表,价格行情_搜料

牌号信息	LEXAN™ HPS6S resin 物性表 PC+ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货	ASTALOY™ PC/ABS EHA 物性表 PC+ABS & 澳大利亚玛佩斯指导价格：暂无塑料库存：缺货
牌号简介	中低流动性聚碳酸酯，用于医疗器械和药物的应用，具有生物相容(ISO10993或USPClass VI). 用于蒸汽、电子束和伽玛灭菌，与HPS6相比，有更高的脱模剂 Medium-low flow polycarbonate for medical device and pharmaceutical applications, biocompatible (ISO10993 or USP Class VI). For steam, electron beam, and gamma sterilization, contains higher mold release agent compared to HPS6.	ASTALOY™ PC/ABS EHA是一种由ABS和聚碳酸酯制成的可电镀合金，设计用于注塑应用，需要平衡易选性、冲击韧性、产品刚度、耐热性和可塑性。汽车领域的典型应用包括电镀格栅、装饰和门把手。注：字母“U”或“W”表示已添加紫外线稳定[即：ASTALOY™ PC/ABS EHA7W]。 ASTALOY™ PC/ABS EHA is an electroplatable alloy of ABS and Polycarbonate and is designed for injection moulding applications requiring a balance of easy electoplatability, impact toughness, product rigidity, heat resistance and mouldability. Typical applications in the automotive field include electroplated grilles, garnishes and doorhandles. Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS EHAW ].

产品描述
厂家：	沙特沙伯基础 SABIC	澳大利亚玛佩斯 Marplex
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：
用途：	制药应用,医疗器械	把手,汽车领域的应用
性能特点：	生物兼容性 Biocompatible	耐候抗UV,易加工,冲击性能好,电镀,耐热性好,防火阻燃等级HB Weather resistance is good,Excellent Processability,High impact resistance,Electroplating,Heat Resistance, Good,HB
加工条件：		注射成型 Injection Molding

技术参数

机械性能
MECHANICAL LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位
UNIT 测试方法
TEST METHOD

弯曲强度(0.45 MPa)
Flexural Strength ℃ ASTM D 648

弯曲强度(1.8MPa)
Flexural Strength ℃ ASTM D 648

弯曲强度(3.20 mm)
Flexural Strength MPa ASTM D790

弯曲强度(屈服，1.30 mm/min，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量(1.30 mm/min，50 mm跨距)
Flexural Modulus MPa ASTM D790

弯曲模量(3.20 mm)
Flexural Modulus MPa ASTM D790

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸应变(断裂，I型，50 mm/min)
Tensile strain % ASTM D638

拉伸强度(3.20 mm)
tensile strength MPa ASTM D638

拉伸强度(屈服，I型，50 mm/min)
tensile strength MPa ASTM D638

拉伸强度(断裂，I型，50 mm/min)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位
UNIT 测试方法
TEST METHOD

仪器冲击能量峰值(23℃)
Instrument impact energy peak N.m ASTM D 3763

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D4812

悬臂梁缺口冲击强度(3.2mm)
Izod Notched Impact strength J/m ASTM D256

落锤冲击(3.2 mm)
Gardner Impact J ASTM D3029

热性能
THERMAL LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，12.7 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
HDT ℃ ASTM D648

热变形温度(未退火，6.4 mm)
HDT

线性热膨胀系数(MD)
Coeff.of linear therm expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temperature ℃ ASTM D1525

维卡软化温度
Vicat Softening Temperature ℃ ASTM D1525 4

物理性能
PHYSICAL LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water Absorption % ASTM D570

密度
Density ASTM D792

密度
Density g/cm³ ASTM D792

收缩率(MD：3.0 mm)
Shrinkage % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage % 内部方法

熔体质量流动速率(250℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(260℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

阻燃性能
FLAMMABILITY LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝起燃温度(1.6 mm)
Glow Wire Ignitability Temperature(GWIT) ℃ AS/NZS 60695.2.12

加工方式

注塑成型 LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位测试方法

中段2区温度 °C

前段3区温度 °C

后段1区温度 °C

喷嘴温度 °C

射到气缸尺寸 %

干燥时间 hrs

干燥时间累计 hrs

干燥温度

排气槽深度 mm

最大含水量 %

模温 °C

熔体温度 °C

背压 MPa

螺杆转速 rpm

注射 LEXAN™ HPS6S resin ASTALOY™ PC/ABS EHA 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 0,051 in/min

4 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
机械性能
冲击性能
热性能
物理性能
阻燃性能
加工方式
注塑成型
注射
备注