生物可降解聚合物，Solanyl® C8103对比生物可降解聚合物，Solanyl® C1203物性表,价格行情_搜料

牌号信息	Solanyl® C8103 物性表生物可降解聚合物 & 荷兰Rodenburg 指导价格：暂无塑料库存：缺货	Solanyl® C1203 物性表生物可降解聚合物 & 荷兰Rodenburg 指导价格：暂无塑料库存：缺货
牌号简介	Solanyl® C8103是一种适用于薄膜应用的端部化合物，专门用于包装。Solanyl® C8103可在适合（多层）柔性薄膜的传统吹塑或铸膜挤出生产线上加工。Solanyl® C8103是目前广泛应用的生物塑料和低密度聚乙烯的竞争替代品。Solanyl® C8103具有自然的感觉和外观，可生物降解，植物源性含量大于40%，生物基碳含量约为30%。Solanyl® C8103可用于：（快餐）包装和消费品运输和垃圾袋一次性可处置农业产品的短寿命可生物降解产品。 Solanyl® C8103 is an end compound suitable for film applications and is specially developed for packaging. Solanyl® C8103 can be processed on conventional blown or cast film extrusion lines suitable for (multi-layer) flexible films. Solanyl® C8103 is a ompetitive alternative for currently used bioplastics and LDPE for a wide range of applications. Solanyl® C8103 has a natural feel and look, is biodegradable and has a plant derived content of >40% with biobased carbon at ~30%. Applications in which Solanyl® C8103 can be used are: (Fast food) Packaging & Consumer goods Carrier & refuse bags Short life biodegradable products for single use disposables Agriculture products	Solanyl® C1203是一种适用于注塑和压缩成型应用的端部化合物。Solanyl® C1203可在常规生产线上加工。Solanyl® C1203是目前广泛应用的可生物降解塑料和聚烯烃的竞争替代品。Solanyl® C1203拥有自然的感觉和外观。Solanyl® C1203可生物降解，生物基和植物基含量大于28%。 Solanyl® C1203 is an end compound suitable for injection & compression molding applications. Solanyl® C1203 can be processed on conventional lines. Solanyl® C1203 is acompetitive alternative for currently used biodegradable plastics & polyolefins for a wide range of applications. Solanyl® C1203 has a natural feel & look. Solanyl® C1203 is biodegradable with a biobased and plant based content of > 28%.

产品描述
厂家：	荷兰Rodenburg	荷兰Rodenburg
类别：	生物可降解聚合物生物可降解聚合物	生物可降解聚合物生物可降解聚合物
填料：
用途：	袋子,包装,流延薄膜,农业应用,食品包装,吹膜
性能特点：	韧性好,热封性好,易剥离,可回收,印刷性好,生物可降解,食品接触,耐油,耐汽油 Good flexibility,Good heat sealing,Good dissection,Renewable resources,Good Printability,Biodegradable,Food contact compliance,Grease resistance,Gasoline resistance	可回收,生物可降解 Renewable resources,Biodegradable
加工条件：	吹塑薄膜	注射成型 Injection Molding

技术参数

薄膜
Solanyl® C8103 Solanyl® C1203 单位
UNIT 测试方法
TEST METHOD

埃尔曼多夫抗撕强度(MD)
Elmandorf tear strength N

埃尔曼多夫抗撕强度(TD)
Elmandorf tear strength N

拉伸应变(MD，屈服)
Tensile strain %

拉伸应变(MD，断裂)
Tensile strain %

拉伸应变(TD，屈服)
Tensile strain %

拉伸应变(TD，断裂)
Tensile strain %

拉伸强度(MD)
tensile strength MPa

拉伸强度(MD，屈服)
tensile strength MPa

拉伸强度(TD)
tensile strength MPa

拉伸强度(TD，屈服)
tensile strength MPa

拉伸模量(MD)
Tensile modulus MPa

拉伸模量(TD)
Tensile modulus MPa

落锤冲击
Drop hammer impact g ASTM D1709

薄膜厚度(测试)
film thickness µm

冲击性能
IMPACT Solanyl® C8103 Solanyl® C1203 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(注塑)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(注塑)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(注塑成型)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(注塑成型)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Solanyl® C8103 Solanyl® C1203 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ 内部方法

玻璃化转变温度
Glass transition temperature ℃ DSC

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

补充信息
Solanyl® C8103 Solanyl® C1203 单位
UNIT 测试方法
TEST METHOD

Water Activity
Water Activity 内部方法

物理性能
PHYSICAL Solanyl® C8103 Solanyl® C1203 单位
UNIT 测试方法
TEST METHOD

含水量
water content % 内部方法

含水量
water content 内部方法

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % ISO 294-4

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体密度
Melt density g/cm³ ISO 1133

熔体表观粘度(140℃，10.0 sec^-1)
Apparent viscosity of melt Pa·s

熔体表观粘度(140℃，100 sec^-1)
Apparent viscosity of melt Pa·s

熔体表观粘度(140℃，1000 sec^-1)
Apparent viscosity of melt Pa·s

熔体表观粘度(170℃，10.0 sec^-1)
Apparent viscosity of melt Pa·s

熔体表观粘度(170℃，100 sec^-1)
Apparent viscosity of melt Pa·s

熔体表观粘度(170℃，1000 sec^-1)
Apparent viscosity of melt Pa·s

熔体质量流动速率(170℃，2.16kg)
Melt Flow Rate g/10min

熔体质量流动速率(170℃，2.16kg)
Melt Flow Rate g/10min 内部方法

熔体质量流动速率(190℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 60

颗粒大小
Particle size mm 内部方法

机械性能
MECHANICAL Solanyl® C8103 Solanyl® C1203 单位
UNIT 测试方法
TEST METHOD

弯曲强度(注塑成型)
bending strength MPa ISO 178

弯曲模量(注塑成型)
Bending modulus MPa ISO 178

拉伸应变(屈服，注塑成型)
Tensile strain %

拉伸应变(断裂，注塑成型)
Tensile strain %

拉伸强度(注塑成型)
tensile strength MPa ISO 527-2

拉伸模量(正割，注塑成型)
Tensile modulus MPa

拉伸模量(注塑成型)
Tensile modulus MPa

邵氏硬度(邵氏 D，注塑成型)
Shore hardness ISO 868

备注