PP均聚，INNOPOL® PP CS 1-7120对比PP均聚，WPP PP PPH1TF2-Black物性表,价格行情_搜料

牌号信息	INNOPOL® PP CS 1-7120 物性表 PP均聚 & 匈牙利Inno-Comp 指导价格：暂无塑料库存：缺货	WPP PP PPH1TF2-Black 物性表 PP均聚 & 美国Washington 指导价格：暂无塑料库存：缺货
牌号简介	Innopol CS 1-7120是一种20%滑石填充聚丙烯均聚物。该等级有自然色和定制色两种形式。推荐应用Innopol CS 1-7120用于板材和型材的挤压，其中一个要求的性能是良好的刚度。 INNOPOL ® CS 1-7120 is a 20 % talc-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 1-7120 is recommended for extrusion of sheets and profiles, where one of the required properties is good stiffness.	WPP PP PPH1TF2-Black是一种聚丙烯均聚物(PP Homopoly)产品,含有的填充物为20% 滑石填料。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。典型应用领域为:汽车行业。主要特性为:耐热。 WPP PP PPH1TF2-Black is a Polypropylene Homopolymer (PP Homopolymer) product filled with 20% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Primary characteristic: heat resistant.

产品描述
厂家：	匈牙利Inno-Comp	美国Washington
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	滑石粉 20	滑石粉 20
用途：	型材,片材	汽车领域的应用
性能特点：	机械强度好,均聚物 Good Rigidity,Homopolymer	耐老化 Good heat aging resistance
加工条件：	片材挤出成型

技术参数

物理性能
PHYSICAL INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(10℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

加工方式

注射 INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度 INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位测试方法

挤出 INNOPOL® PP CS 1-7120 WPP PP PPH1TF2-Black 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

熔体温度 °C

备注

2 2.0 mm/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.050 in/min

4 0.079 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
注射速度
挤出
备注
返回顶部