环氧树脂，BCC Products BC7053对比环氧树脂，Ebalta GH 730 / BR物性表,价格行情_搜料

牌号信息	BCC Products BC7053 物性表环氧树脂 & 美国BCC Products 指导价格：暂无塑料库存：缺货	Ebalta GH 730 / BR 物性表环氧树脂 & 德国Ebalta 指导价格：暂无塑料库存：缺货
牌号简介	BC 7053是一种充铁环氧浇注系统。该系统是一种高铁含量材料，具有无与伦比的耐磨性。BC7053设计用于建造芯盒、固定和修整夹具、铸造模具等。 BC 7053 is an iron filled epoxy casting system. This system is a high iron content material that provides unsurpassed wear resistance. BC7053 was designed for use in constructing core boxes, holding and trimming fixtures, foundry patterns, etc.	EBALTA GH 730/BR是一种用途广泛的双组分环氧树脂，具有良好的浇注性，室温固化。由于其易加工性以及高强度和低收缩性，在模具制造、工具制造和铸造中有着广泛的应用。此外，高抗冲击性和超过30毫米的铸造厚度使更多的应用成为可能。应用铸造型芯盒夹具性能耐冲击多用途 ebalta GH 730/BR is a quite versatile two-components epoxy resin with good castability, curing at room temperature. Due to its easy workability as well as its high strength and low shrinkage there's a big variety of applications as mouldmaking, toolmaking and in foundries. Moreover the high impact resistance and cast thickness of more than 30 mm make even more applications possible. Applications Foundry patterns Core boxes fixtures Properties impact resistant versatile

产品描述
厂家：	美国BCC Products	德国Ebalta
类别：	环氧树脂环氧树脂	环氧树脂环氧树脂
填料：
用途：	模板
性能特点：	可分散,耐磨 Machinable,Good wear resistance	机械强度好,冲击性能好,收缩性低 Good Rigidity,High impact resistance,Low contractility
加工条件：	浇铸 casting	浇铸 casting

技术参数

物理性能
PHYSICAL BCC Products BC7053 Ebalta GH 730 / BR 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³

收缩率
Shrinkage rate % 内部方法

收缩率(MD)
Shrinkage rate % ASTM D2566

热性能
THERMAL BCC Products BC7053 Ebalta GH 730 / BR 单位
UNIT 测试方法
TEST METHOD

热变形温度
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热固组件(树脂)
Thermosetting components

热固组件(硬化法)
Thermosetting components

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：20~50℃)
Linear coefficient of thermal expansion 1/℃ DIN 53752

Uncured Properties
BCC Products BC7053 Ebalta GH 730 / BR 单位
UNIT 测试方法
TEST METHOD

体积混合比(PBV)(Hardener)
Volume Mixing Ratio (PBV)

体积混合比(PBV)(Resin)
Volume Mixing Ratio (PBV)

储存稳定性(20 ℃)
storage stability min

储存稳定性(24 ℃)
storage stability min

固化时间(20℃)
Curing time hr

固化时间(24℃)
Curing time hr

密度(20℃)
Density g/cm³

粘度(25℃)
viscosity Pa·s

粘度(布络克菲尔德，24℃)
viscosity Pa·s

重量混合比(PBW)(Hardener)
Weight Mix Ratio (PBW)

重量混合比(PBW)(Resin)
Weight Mix Ratio (PBW)

Cured Properties
BCC Products BC7053 Ebalta GH 730 / BR 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa

弯曲断裂强度
Bending fracture strength MPa

拉伸断裂强度
Tensile fracture strength MPa

邵氏硬度(邵氏 D，24℃)
Shore hardness

冲击性能
IMPACT BCC Products BC7053 Ebalta GH 730 / BR 单位
UNIT 测试方法
TEST METHOD

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

机械性能
MECHANICAL BCC Products BC7053 Ebalta GH 730 / BR 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ISO 604

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

泰伯耐磨性(500 周期，500 g，CS-17 转轮)
Taber abraser mg 内部方法

邵氏硬度(邵氏 D)
Shore hardness ISO 7619

备注

2、Mixed

1 一般属性：这些不能被视为规格。

2 200 g


相关资讯

牌号简介
产品描述
技术参数
物理性能
热性能
Uncured Properties
Cured Properties
冲击性能
机械性能
加工方式
备注
返回顶部