PP均聚，OnForce™ LFT PP-40LGF-000 8001 UV对比PP均聚，RTP 107CC HS物性表,价格行情_搜料

牌号信息	OnForce™ LFT PP-40LGF-000 8001 UV 物性表 PP均聚 & 美国普立万指导价格：27090.0元/吨塑料库存： 5000kg	RTP 107CC HS 物性表 PP均聚 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	PolyOne的长纤维热塑性塑料（LFT）化合物适用于需要高刚度和良好冲击的苛刻应用，作为金属替代品或其他结构应用。这些产品与标准短玻纤维制品相比具有增强的物理和机械性能。 LFT化合物的优点包括在较宽温度范围内提高冲击强度，弹性模量和材料强度。此外，LFT化合物已经显示出在蠕变和抗疲劳领域具有良好的性能，尺寸稳定性，并且与传统的高填充短纤维产品相比，表现出优异的表面光洁度。 "PolyOne's Long Fiber Thermoplastic (LFT) compounds are suitable for demanding applications requiring high stiffness and good impact, serving as metal replacement or other structural applications. These products have enhanced physical and mechanical properties compared to standard short glass fiber products. Advantages of LFT compounds include improved impact strength, modulus, and material strength over a wide temperature range. Additionally, LFT compounds have shown good performance in creep and fatigue resistance, dimensional stability, and exhibit excellent surface finish compared to conventional highly filled short fiber products."	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。-每个RTP公司的初步产品数据- Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.-

产品描述
厂家：	美国普立万 Polyone	美国RTP
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：
性能特点：	机械强度好,冲击性能好,玻纤增强 Good Rigidity,High impact resistance,Glass fiber reinforced	化学耦合,热稳定性好,防火阻燃等级HB Chemical coupling,Heat Stabilized,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water Absorption % ASTM D570

密度
Density ASTM D792

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage % ASTM D955

机械性能
MECHANICAL OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位
UNIT 测试方法
TEST METHOD

弯曲强度
Flexural Strength MPa ASTM D790

弯曲模量
Flexural Modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位
UNIT 测试方法
TEST METHOD

仪表落镖冲击(-20℃，3.18 mm，总能量)
Instrument drop dart impact J ASTM D3763

仪表落镖冲击(-20℃，3.18 mm，能量最大负载)
Instrument drop dart impact J ASTM D3763

仪表落镖冲击(23℃，3.18 mm，总能量)
Instrument drop dart impact J ASTM D3763

仪表落镖冲击(23℃，3.18 mm，能量最大负载)
Instrument drop dart impact J ASTM D3763

悬臂梁无缺口冲击强度(3.2 mm)
Izod Unnotched Impact strength J/m ASTM D4812

悬臂梁缺口冲击强度(23℃，3.18 mm)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度()
Izod Notched Impact strength J/m ASTM D256

热性能
THERMAL OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
HDT ℃ ASTM D648

线性膨胀系数-流动(-30 -30℃，3.18 mm)
Linear expansion coefficient - flow (-30-30 ℃, 3.18 mm) cm/cm/℃ ASTM D696

电气性能
ELECTRICAL OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

阻燃性能
FLAMMABILITY OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注塑成型 OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位测试方法

干燥温度 °C

注射 OnForce™ LFT PP-40LGF-000 8001 UV RTP 107CC HS 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注塑成型
注射
备注
返回顶部