牌号简介 About |
---|
UNITHENE LH606是一种高密度聚乙烯(HDPE),适用于注塑和长丝应用。典型的应用是水果箱,食品容器,工业物品如托盘,运输箱,家庭用品,玩具和蚊帐细丝挤出的注塑成型。UNITHENE LH606具有高冲击强度和良好的抗应力开裂性,良好的刚性,高硬度,良好的表面光泽,较少的翘曲,低收缩率。通过干混或将颜料熔融混合到树脂中,UNITHENE LH606可轻松着色成任何颜色。在简单的火焰,化学或电子表面处理之后,可以轻松地在UNITHENE LH606模塑件上进行印刷 UNITHENE LH606 is a high density polyethylene (HDPE) suitably used for injection molding and filament applications. Typical applications are the injection molding of fruit crates, food containers, industrial items such as pallets, transportation crates, housewares, toys and the fine filament extrusion of mosquito nets. UNITHENE LH606 possesses high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage. UNITHENE LH606 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. Printing on items molded from UNITHENE LH606 can be easily accomplished after a simple flame, chemical or electronic surface treatment. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.962 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
6.0 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
69 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -76.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
127 | ℃ | ASTM D1525 |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
|||
1% 正割,模压成型 1% cut, molded |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D747 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 I (三点负荷) |
【新闻资讯】查看全部
金路集团氯乙烯事故 三人中毒身亡
2016-03-17 四川金路集团公司下属全资子公司四川省金路树脂有限公司树脂分厂实验室人员3月16日上午在清釜过程中发生氯乙烯中毒事故,三人身亡。 金路集团 金路集团表示,公司正 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |