牌号简介 About |
---|
Alkamax ML1810PN是一种茂金属线性低密度聚乙烯共聚物。这种茂金属品位具有良好的加工性能,可提高生产率。它是为高性能薄膜应用而设计的,要求最大的韧性和良好的密封性能。Alkamax ML1810PN采用工艺助剂和工艺稳定包配制而成。不含防滑或防堵塞添加剂。Alkamax ML1810PN适用于需要高性能聚乙烯树脂的应用。用Alkamax ML1810PN生产的薄膜具有优异的韧性,使其非常适合用于重型应用或对现有薄膜结构进行下测。此外,该等级的高性能密封和热粘性能结合其优良的光学性能,使其成为层压和成型、填充和密封薄膜的理想选择。它被设计用于各种吹塑薄膜挤出设备的加工。如果预期的应用涉及间歇性到长时间暴露在阳光下,则应考虑添加紫外线稳定剂。 Alkamax ML1810PN is a metallocene linear low density polyethylene copolymer. This metallocene grade has excellent processability permitting higher production rates. It is designed for high performance film applications requiring maximum toughness and excellent sealing performance. Alkamax ML1810PN is formulated with a process aid and process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: Alkamax ML1810PN is intended for applications requiring high performance polyethylene resins. Films produced with Alkamax ML1810PN have outstanding toughness, making this grade ideal for use in heavy duty applications or for downgauging existing film structures. In addition, the high performance sealing and hot tack properties of this grade combined with its excellent optical properties make it ideal for lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
割线模量 Secant modulus 2 |
ASTM D882 | ||
2% 正割,MD:50 µm 2% secant, MD: 50 µ m |
183 | MPa | ASTM D882 |
2% 正割,TD:50 µm 2% secant, TD: 50 µ m |
190 | MPa | ASTM D882 |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服,50 µm MD, yield, 50 µ m |
MPa | ASTM D882 | |
TD,屈服,50 µm TD, yield, 50 µ m |
MPa | ASTM D882 | |
MD,断裂,50 µm MD, fracture, 50 µ m |
MPa | ASTM D882 | |
TD,断裂,50 µm TD, fracture, 50 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,断裂,50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
TD,断裂,50 µm TD, fracture, 50 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 4 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:50 µm MD:50 µm |
g | ASTM D1922 | |
TD:50 µm TD:50 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss 5 |
|||
45° 45° 5 |
ASTM D2457 | ||
雾度 Haze 5 |
|||
50 µm 50 µm 5 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.79 in/min |
3 20 in/min |
4 F50 |
5 (10% LDPE blended) |
【新闻资讯】查看全部
总投资300亿元!河南新建煤化工项目
2022-04-14 近年来,汝州市坚持制造业高质量发展主攻方向,大力支持传统煤炭焦化产业升级改造,建立精细化工产业园区,积极开展延链补链强链,加快形成原煤-焦化-精细化工的完整产业链, |
总投资300亿元!河南新建煤化工项目 近年来,汝州市坚持制造业高质量发展主攻方向,大力支持传统煤炭焦化产业升级改造,建立精细化工产业园区,积极开展延链补链强链,加快形成“原煤-焦化-精细化工”的完整产业链,推动精细煤化工产业绿色化、集聚化、高端化发展。
依托上游传统原煤优势资源,加快绿色大型发展。汝州市现有煤炭储量约35亿吨,是全国主焦煤生产基地之一。全市原煤开采企业共13家,产能826万吨,年产150万吨原煤的平煤集团夏店矿正在试生产;焦化企业每年可产2.7亿立方煤气;朝川矿一井年产180万吨主焦煤,是全省第二大主焦煤基地,为汝州煤焦化产业发展提供了充足煤炭资源支撑。 聚焦中游煤炭焦化主导产业,加快转型集聚发展。围绕焦炉煤气、煤焦油、电石、电石尾气打造“吃干榨净”式的煤炭焦化全产业链。利用汝丰、天瑞煤焦化未来600万吨焦炭产能,建设国内一流的绿色、低碳、智能碳基新材料产业园。利用汝州600万吨焦炭、90万吨电石、40万吨煤焦油和20亿立方米焦炉煤气等优势产能资源,全力支撑精细化工产业园区建设,计划总投资300亿元,其中焦化企业项目投资100亿元,下游化工项目投资200亿元。
瞄准下游精细化工产业方向,加快高端升级发展。围绕煤焦化优势,初步绘制了精细化工产业“四张图谱”,计划开展“四个拜访”活动。在此基础上,利用现有的煤气和煤焦油资源,通过积极与平煤集团对接合作,延长产业链条,将产品向新能源、新材料延伸,从4个产业链方面进行谋划: 一是利用焦化企业和汝州电化资源打造1,4丁二醇产业链。 二是利用焦化板块和汝州电化尾气资源打造碳酸二甲酯产业链。 三是打造精细化工产业链。谋划实施生物降解塑料原材料1,4丁二醇、20万吨合成氨、聚氨酯弹性体、碳酸二甲酯等项目。 四是打造高端钙系列产业链。 谋划项目建成后,精细化工产业园区年营业收入达500亿元,从业人员1.5万人,利税突破65亿元,形成涵盖从上游基础原料、中间体,到下游新材料的完整产业链,实现闭环发展,成为国内领先的绿色低碳新材料基地。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。