PA 6,30%玻璃纤维/碳纤维,注塑成型,热老化稳定,提高导电率 Durethan® BCF30XH3.0 901510 DUS040 (Dry) PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 901510 DUS040 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 901510 DUS040 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm |
0.10 | % | |
TD:280℃,2.0 mm TD:280℃,2.0 mm |
0.70 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm |
0.050 | % | |
MD:280℃,2.0 mm MD:280℃,2.0 mm |
0.20 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
|||
-30℃,冲击总贯穿能量 -30 ℃, total impact penetration energy |
J | ||
23℃,冲击总贯穿能量 23 ℃, total impact penetration energy |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 600 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |